文档介绍：学生学业论文
题目: 焊接检验技术
年级班级:
学生姓名:
学号:
指导教师:
目录
摘要·····························································2
一、焊接的检验过程和质量控制
一、焊接检验······················································3
二、焊接过程中的质量控制··········································3
三、焊接成品结构的检验············································4
二、射线探伤
一、射线的产生、性质及衰减········································5
二、射线探伤原理··················································5
三、焊接射线底片的评定···········································6
三、超声波的探伤
一、超声波探伤的原理及应用
········································7
二、缺陷定位与缺陷性质估判········································7
四、磁粉探伤
一、磁粉探伤原理··················································8
二、磁粉探伤过程··················································8
三、缺陷判别························································8
五、结束语····························································9
六、主要参考文献··················································10
摘要
本文主要讲述焊接生产检验过程及各种无损探伤方法的基本原理、探伤过程及应用。
焊接的检验过程和质量控制主要介绍了焊接方面的基础知识、焊接材料、焊接接头形式及焊接代号、焊接方法及熔焊原理、焊接应力与变形、焊接质量控制及检验方法、焊接缺陷产生原因和预防措施、焊接工艺评定等内容,具有一定的先进性和实用性
射线探伤利用 X射线或γ射线在穿透被检物各部分时强度衰减的不同,检测被检物中缺陷的一种无损检测方法。被测物体各部分的厚度或密度因缺陷的存在而有所不同。当X射线或γ射线在穿透被检物时,射线被吸收的程度也将不同。
超声波的探伤利用材料及其缺陷的声学性能差异对超声波传播的影响来检验材料内部缺陷的无损检验方法。现在广泛采用的是观测声脉冲在材料中反射情况的超声脉冲反射法,此外还有观测穿过材料后的入射声波振幅变化的穿透法等。~5MHz之间。
磁粉探伤可用来作最后的成品检验,以保证工件在经过各道加工工序(如焊接、金属热处理、磨削)后,在表面上不产生有害的缺陷。它也能用于半成品和原材料如棒材、钢坯、锻件、铸件等的检验,以发现原来就存在的表面缺陷。铁道、航空等运输部门、冶炼、化工、动力和各种机械制造厂等,在设备定期检修时对重要的钢制零部件也常采用磁粉探伤,以发现使用中所产生的疲劳裂纹等缺陷,防止设备在继续使用中发生灾害性事故。
关键字:缺陷定位与缺陷性质估判、焊接检验、焊接质量、射线探伤、超声波的探伤、磁粉探伤、焊接成品结构的检验·
一、焊接的检验过程和质量控制
焊接检验贯穿焊接全过程,但各个生产环节要检验的内容不一样,重点介绍各生产环节应检验的内容、检验的方法和检验的标准。产品的质量是企业的生命。建造质量是保证作业的重要条件。结构强度要求焊缝保证一定的强度,能承受强冲击。如果焊接接头存在严重的焊接缺陷,在恶劣的环境下,就有可能造成部分结构断裂;甚至引起重大事故。据对船舶脆断事故调查表明,40%的脆断事故是从焊缝缺陷处开始的。焊接产品的质量方面存在的主要问题就是焊缝质量的缺陷。因此,焊接质量检验尤为重要,做到及早发现焊接缺陷,对焊接接头的质量做出客观的评价;把焊接缺陷限制在一定的范围内,以确保设备安全和人命财产安全。
一、焊接检验
焊接检验是指对焊接结构及其生产过程的检验,其检验的内容不仅包括对焊缝和焊接接头的质量检验,而且包括制造该产品的原材料、生产人员、采用的设备、制定的工艺方法和生产环境的检验;以及对焊接产品