文档介绍：安徽大学
本科毕业论文
题目:细乳液聚合法制备纳米TiO2/丙烯酸酯共聚物的
研究
学生姓名: 学号:
细乳液聚合法制备纳米TiO2/丙烯酸酯共聚物的研究
摘要
本文首先使用甲基丙烯酸-3-三甲氧基硅烷(KH-570)对纳米TiO2粒子进行偶联处理,进一步通过细乳液聚合得到了内部包裹纳米TiO2粒子的核-壳型复合粒子。通过热重分析(TG)表征,%~%的K H-570;通过探讨乳化剂、助稳定剂用量与转化率的关系,结果显示:温度应控制在70℃,乳化剂用量为单体用量的2%,助乳化剂(HD)用量选为单体用量的3%时,可以得到稳定的胶粒粒径分布较窄的细乳液;通过吸水率、拉伸强度和热重分析测试,表明纳米TiO2可以提高聚合物的耐水性、耐候性和拉伸强度。
关键词:细乳液聚合;纳米TiO2;水性丙烯酸酯;KH-570;
Preparation of titanium dioxide/acrylate polymer
posite particles via miniemulsion polymerization
Abstract
In this paper, nano-TiO2 particles was modified by 3-(trimethoxysilyl)- propyl- methacrylate(KH-570), and further the core-posite particles was preparation via miniemulsion polymerization. Thermogravimetric analysis (TG) characterization showed the encapsulation efficiency of nano-TiO2 was about % ~ % with the KH-570; and the relationships of the amount of emulsifier, stabilizer and the con- version were discussed,the results showed that: the temperature should be controlled at 70℃, when the content of emulsifier was 2% of the monomer and costabilizer(HD) was 3%, the particles can be stable with narrow particle size distribution; Besides, the water-absorbing ratio, pull extensor strength and TG tests showed that nano-TiO2 can increase the water resistance, weather resistance and tensile strength of the polymer.
Key words: miniemulsion polymerization; nano-TiO2; acrylate polymer; 3-(trimeth- oxysilyl)propyl methacrylate
目录
第一章前言 1
水性丙烯酸酯树脂的研究进展 1
水性丙烯酸酯纳米复合物的进展 1
聚合方法的选择 2
本实验方法的简介 3
实验步骤简介 3
反应机理 3
第二章实验部分 4
实验原料 4
纳米TiO2粒子表面处理 4
单体细乳液的制备 4
细乳液聚合 4
性能测试 4
单体转化率 4
聚合过程稳定性 4
胶膜吸水性 4
力学性能 5
热重分析 5
红外光谱表征 5
粒子形貌 5
第三章结果与讨论 6
红外谱图 6
热分析 6
纳米TiO2热重分析 6
聚合物热重分析 7
温度对转化率的影响 8
乳化剂(SDS)用量对转化率的影响 9
助乳化剂(HD)用量对聚合反应的影响 9
应力-应变曲线 10
二氧化钛用量对聚合物膜吸水率的影响 10
改性后TiO2粉体和复合物胶粒的形貌(TEM) 11
第四章结论 13
主要参考文献 14
致谢 15
第一章前言