文档介绍：电池工业
第 l7卷第 1期 2012年 2月
废旧锂离子电池中铝资源回收工艺研究
刘更好,周汉章,唐红辉,谭静进
(佛山市邦普循环科技有限公司研发部,广东佛山 528244)
摘要:实验研究了废旧锂离子电池再生过程中铝资源回收工艺,考察不同氢氧化钠用量、液固比及浸
出段数对铝浸出率的影响。结果表明氢氧化钠用量为理论值 1-3倍、液固比为 4、选用两段浸出,铝浸
出率可达到 %;在pH值为 8的条件下,氢氧化铝的沉淀率为 %。
。
关键词:废旧锂离子电池;金属回收;铝
中图分类号: 文献标志码:A 文章编号:1008—7923(2012)01—0017—03
Researchon the technology ofrecovering aluminum
from spentLi-ion batteries
LIUGeng-hao,ZHOU Han—zhang,TANG Hong—hui,TAN Jing-jin
(FoshanBrunp RecyclingTechnology Co.,Ltd.,Fo$holl,~Guangdong 8244,China)
Abstract:The technology ofrecovering aluminum from spent Li—ion batterieswas studied
The influence ofdifferent operation parameters was investigated,such as the amountNaOH,the of ratio
ofliquid solid,andto the leaching results indicated that,when the amount of NaOH was
times of stoichiometric ratio,the ofratio liquid solidto was 4,and 2-section leaching was used,the
aluminum leaching rate was % .At pH % ofalumina could be deposited from the leaching
solution.
Key words:spentLi-ion battery;metalregeneration;aluminum
随着锂离子电池广泛应用,产量和消费量都逐流体,被广泛用于锂离子电池中。在废旧锂离子电池
年攀升。据报道,2009年全球锂电池产销量达 31亿回收过程中必须将铝除干净,才能实现废旧锂离子
只,并将保持较强增长态势【l】。同时,每年锂电池报废电池中有价金属的高效回收。由于铝元素在废旧锂
量也不断增加,必将给环境和资源造成巨大的压力, 离子电池废料中含量较高,在除铝工艺中[9-砌,采用中
废旧锂电池的再生能实现资源再生,并具有很好的和法和萃取法除铝效果不理想,本文重点研究在碱
环境效益和经济效益[2-31。浸除铝工艺,通过调节碱浸除铝工艺参数,提高碱浸