Ni3 Al金属间化合物纳米粒子的制备及表征
张延峰。郝春成。
(青岛科技大学材料科学与工程学院,山东青岛266042)
摘
要:以镍铝金属块为原料,利用氢电弧等离子体法制备出的产物经X射线衍射
(XRD)表征,证明产物为结晶性好的Ni。Al纳米粒子。通过透射电镜(TEM)观察发现,
粒子多为球形,其粒径在5"--50 nm之间。实验发现。在一定范围内,工作电压越高、氢气
含量越高,纳米Ni。Al产率越高。在氮气气氛下对产物进行热重分析,结果表明Ni。Al纳
米粒子在800℃氮气气氛下可以稳定存在:
关键词:氢电弧等离子体法;Ni。Al;纳米粒子
中图分类号:TB 321
文献标志码:A
Preparation and Characterization of Nanostructured
Ni3 AI pounds
ZHANG Yan—feng,HAO Chun—cheng
(College
Materials
Engineering,Qingdao
Science
Technology,Qingdao 266042,China)
Abstract:In this study,nanostructured Ni3 A1 pounds were prepared by
hydrogen
discharge product was characterized by transmission electron
microscopy(TEM),X—ray diffraction method(XRD).It was found that the products
mostly crystalline Ni3 AI nanoparticles,with the size of about
5—50
higher op—
crating voltage and the more concentration of hydrogen in
the atmosphere
resulted in
higher the was shown by thermogravimetric analysis(TGA)in nitrogen
atmosphere that the Ni3 AI nanoparticles
stable in nitrogen atmosphere
800℃.
Key words:hydrogen
discharge;Ni3 A1;nanoparticle