文档介绍：本科毕业设计(论文)
VAc/BA/AA三元无皂乳液共聚的研究
Study on Emulsifer -free Emulsion of VAC /BA/AA
2011 年 6 月
毕业设计(论文)中文摘要
VAc/BA/AA三元无皂乳液共聚的研究
摘要:采用无皂乳液聚合方式,以醋酸乙烯酯、丙烯酸丁酯、丙烯酸为单体,过硫酸铵为引发剂制备三元共聚物,探讨了丙烯酸用量、引发剂用量对乳液的转化率、耐水性、含固率、凝胶率以及粒径分布的影响规律。对实验过程中的各种实验现象及数据进行了详细的记录,并对产物进行了红外光谱、粒径分析等测试。
关键词:无皂乳液聚合;聚醋酸乙烯酯;丙烯酸;过硫酸铵;制备
毕业设计(论文)外文摘要
Study on Emulsifer -free Emulsion of VAC /BA/AA
Abstract: The latex particles of VAC /BA/AA were prepared via an emulsifier-free emulsion copolymerization using KPS as an initiator and VAc,BA,AA as monomers .The influence of initiator and functional monomer (AA) on the conversion rate, absorption rate , solid content, gel rate and particle size distribution was studied. In the course of study, experimental phenomena and data are recorded in details, test of infrared spectrum, particle size distribution and other related experiment are conducted to explore the property of the polymer.
Keywords: emulsifier-free emulsion copolymerization; polyvinyl acetate(VAc); acrylic acid(AA); ammonium persulfate (APS); preparation
目录
1 引言 1
乳液聚合 1
聚醋酸乙烯酯乳液的研究与现状 1
无皂乳液 2
无皂乳液的常用聚合方法 3
无皂乳液聚合的应用 4
无皂乳液法制聚醋酸乙烯酯乳液的研究 4
论文的主要研究内容与意义 4
2 实验部分 6
实验装置及仪器 6
实验药品 6
实验原理及步骤 7
实验过程及现象进行记录 9
性能测试 10
3 数据分析与讨论 12
乳液外观目测 12
红外表征 12
凝胶率 13
含固率 14
转化率 15
耐水性 16
机械稳定性 17
稀释稳定性 17
冻融稳定性 17
高温稳定性 17
粒径分布 17
结论 20
致谢 21
参考文献 22
1 引言
乳液聚合
乳液聚合特点
乳液聚合是高分子合成中的一种常用合成方法,一般以水为溶剂,液态的乙烯基单体或二烯烃单体在乳化剂的存在与机械搅拌的作用下分散于水中成为乳状液,并由引发剂引发聚合反应。
乳液聚合与其他自由基聚合反应方法相比有着独特的优点。通常,烯类单体的聚合反应放热量都很大,在生产过程中,不易控制排热,不仅影响了产品的品质,还易造成安全隐患。但是,对乳液聚合过程来说,它的溶剂是水,聚合反应发生的位置也是水相中的乳胶粒眼。这样的反应位置与溶剂使整个体系的粘度保持在较低的水平。这样就使反应过程中的搅拌易于进行,使反应均匀,不会出现暴聚局部过热等现象,且便于管道输送,实现工业生产中的连续化操作。
在烯类单体的自由基聚合中,若以自由基浓度为定量,那么加快反应的唯一途径就是提高反应温度[1]。提高反应温度的结果就是引发剂分解加速链终止提前,最终导致聚合物平均分子量减小。也就是说分子量的增大与反应速率的增大是矛盾的。而乳液聚合可以将二者统一起来,即既有高的反应速率,又可得到高分子量的聚合物[2]。乳液聚合能将高分子反应过程中的两个矛盾统一起来的原因就在于乳液聚合反应独特的聚合机理,聚合反应的引发剂在水相中分解成自由基,并扩散到胶束或乳胶