文档介绍：2010年8月第七届中国热处理活动周论文集秦皇岛高强度铝合金锻件热处理工艺改进刘春燕1;周丹晨;李昌安;曹海桥;郝爱国(中国工程物理研究院机械制造工艺研究所四川绵阳621900) 摘要:对性能不合格的2A14铝合金锻件进行固溶、时效、补充时效处理,处理后检测力学性能及金相。结果表明,时效不充分是引起强度、硬度偏低的主要原因;通过增加固溶保温时间以及时效保温时间、降低淬火冷却水温,有效地改善了锻件力学性能,合理匹配了强度与伸长率的性能数据,使两者均有一定富余量;经过以上工艺改进,提高了锻件热处理批量生产的质量。关键词:2A14铝合金锻件;热处理;力学性能 Improvement ofheattreatment process forhigh strength aluminium alloy LIU Chun—yan;ZHOU Dan—chen;Li Cang—aN;CAO Hai-qiao;HAO Ai—guo Abstract:For mechanical properties being unqualified,2A14 aluminium ings are heat treatment by solution and ageing and re—ageing,mechanical properties and hardness and metallographic ale results show under age- ing the tensilestrength and hardness are lower;By Increasing solutionholding timeand ageing holding - ducing cooling water temperature,mechanical properties are improved。the tensilestrength and elongation percentage are matched rationally withboth having capacity certainly more improvements heattreatment process raise ingsquality massproduction. Keywords:Aluminium ing;heat treatment mechanical properties , 可热处理强化,固溶处理加人工时效后强度高, 因具有优良的热塑性,主要用于生产锻件¨】。某 2A14铝合金零件加工工艺流程为:锻造毛坯-固溶、。其中热处理要求毛坯固溶、时效后解剖同炉处理的平行试样的组织及性能,技术要求曲≥360Mpa、85≥ 4%、HBS≥120,高倍金相组织无过烧。生产中该类铝合金锻件热处理性能不稳定,,影响了产品的按期交付。 1原热处理工艺根据锻件的材料及形状、大小,制定了某2A14 锻件毛坯固溶、时效工艺,原工艺曲线见图1。锻件装入料筐内,到温装炉在90kw井式电阻内固溶加热、保温结束后快