文档介绍：硅烷化处理对烧结钗铁硼永磁材料耐腐 蚀性能的影响
张浩 张鹏杰 曹玉杰 刘家琴 衣晓飞 陈静武 吴玉 程
合肥工业大学工业与装备技术研究院稀土永磁材料 国家重点实验室(安徽大地熊新材料股份有限公司) 合肥工业大学材料科学与工程学院
摘film and substrate is up to 14. 14 MPa. The neutral salt spray test of the silane conversion film can reach 12 h. There are different crosslinking density area formed in the surface of the silane conversion film due to the alcohol-based dehydration and condensation reactions, and the low crosslinking density area firstly dissolved hydrolysis is the main reason of the corrosion failure of the silane conversion film in Na Cl solution.
Keyword：
sintered NdFeB; permanent magnet material; silane conversion film; anticorrosion property; corrosion mechanisni;
Received： 2017-08-02
引用格式:张浩，张鹏杰，曹玉杰， 蚀性能的影响，］.材料热处理学报，2017, 38 (12) : 70-76.
ZHANG Hao, ZHANG Peng-jie, CAO Yu-jie, et al. Effect of silanization treatment on corrosion resistance of sintered Nd Fe B permanent magnets［J］. Transactions of Materials and Heat Treatment, 2017, 38 (12) : 70-76.
烧结Nd Fe B磁体自1983年问世以来，以其优异的磁性能而被广泛应用于电子、 汽车、电力、医疗器械、仪器仪表、航空航天等诸多领域但是，采用粉 末冶金工艺制备的烧结Nd Fe B磁体内部为多相结构，各相之间存在较大的电位 差，在电化学腐蚀环境中易产生电化学腐蚀并最终导致磁体的粉化失效，严重 限制了磁体应用领域的拓展［4-5］。
当前用于提高烧结Nd Fe B磁体耐腐蚀性能的方式主要有两种:一是添加合金元 素法;二是在磁体表面添加防护涂层财］。合金化法提高磁体耐腐蚀性能通常是 以牺牲磁体磁性能为代价的，且磁体耐蚀性能提高的范围有限。因此，当前工业 上通常采用表面添加防护涂层的方式提高磁体的耐蚀性能。防护涂层是通过阻碍 腐蚀介质与基体之间的相互接触来减缓磁体的腐蚀，当前Nd Fe B制造行业对磁 体进行腐蚀防护的方式主要包括磷化、电镀、化学镀、有机涂层的涂覆以及物理 气相沉积等 在汽车电机等磁体应