文档介绍:Hessen was revised in January 2021
焊接技术论文
焊接技术论文
题 目 焊接技术的············2
吸锡器的基本认识························································3
吸锡器的使用方法及注意事项··············································3
····················································3
锡的含量································································3
锡的规格································································4
····················································4
······································5
····················································5
参考文献··················································5
焊接的基本概念
所谓焊接,就是用焊锡作媒介,藉加热而使两金属接连并达到导电的目的。两金属间的接合力即靠焊锡与金属表面产生的合金层,所以焊锡不能当做金属力的支撑,只能作电气传导。
图 1
焊接的条件
(1)焊件必须具有良好的可焊性----被焊物可焊性。不是所有的金属都具有良好的可焊性,有些金属如铬、钼、钨等的可焊性就非常差;有些金属的可焊性又比较好,如紫铜、黄铜等。在焊接时,由于高温使金属表面产生氧化膜,影响材料的可焊性。为了提高可焊性,一般采用表面镀锡、镀银等措施来防止表面的氧化。
(2)焊件表面必须保持清洁。为了使焊锡和焊件达到良好的结合,焊接表面一定要保持清洁。即使是可焊性良好的焊件,由于储存或被污染,都可能在焊件表面产生有害的氧化膜和油污。在焊接前务必把污膜清除干净。否则无法保证焊接质量。
(3)要使用合适的助焊剂。不同的焊接工艺,应选择不同的助焊剂,如镍铬合金、不锈钢、铝等材料,没有专用的特殊焊剂是很难实施锡焊的。在焊接电子线路板等精密电子产品时,为使焊接可靠稳定,通常采用松香助焊剂。一般,将松香溶解成松香水使用。
(4)焊件要加热到适当的温度---热源。需要强调的是,不但焊锡要加热到熔化,而且应该同时将焊件加热到能够熔化焊锡的温度。导线端敷涂一层焊剂,同时也镀上焊锡。要注意,不要让锡浸入到导线的绝缘皮中去,最好在绝缘皮前留出1-3mm的间隔,使这段没镀锡。这样镀锡的导线,对于穿管是很有利的,同时也便于检查导线有无断股。
(5)正确手焊技巧。
电烙铁的分类
电烙铁常用的分为内热式和外热式两种。
外热式电烙铁由烙铁头、烙铁芯、外壳、木柄、电源引线、插头等部分组成。由于烙铁头安装在烙铁芯里面,故称为外热式电烙铁。烙铁芯是电烙铁的关键部件,它是将电热丝平行地绕制在一根空芯瓷管上构成,中间由云母片绝缘,并引出两根导线与220V交流电源连接。外热式电烙铁的规格很多,常用的有15W、25W、30W、40W、60W、80W、100W、150W。 电烙铁功率越大,烙铁头的温度就越高。
内热式电烙铁由手柄、连接柄、弹簧夹、烙铁芯、烙铁头组成。由于烙头组成。由于烙铁芯安装在烙铁里面,因而发热快,热利用率高,因此,称为内热式电烙铁。内热式电烙铁的常用规格为20W,50W等几种,由于它的热效率较高,20W内热式电烙铁就相当于40W左右的外热式电烙铁。内热式电烙铁头的后端是空心的,用于套接在连接杆上,并且用弹簧夹固定,当需要更换烙铁头时,必须先将弹簧夹退出,同时用钳子夹住烙铁头的前端,慢慢地拔出,切记不能用力过猛,以免损坏连接杆。内热式电烙欣的烙铁芯是用比较细的镍铬电阻丝绕在瓷管上制成的其电阻约为Ω左右(20W),烙铁的温度一般可达350℃左右。
由于内热式电烙铁的烙铁有升温快、重量轻、耗电小、体积小、热效率高的特点,因而得到了普遍的应用。
电烙铁使用及注意事项
电烙铁的握法基本有两种。一种是满手抓住手柄,实握。这种方法适合初