文档介绍：浅析斜拉桥中斜拉索病害的构成
浅析斜拉桥中斜拉索病害的构成
[摘要]斜拉桥虽具有跨越能力大、结构型式简洁、受力明确、空气动力稳定性好、结构轻巧美观等优点,但拉索腐蚀退化和疲劳抗力衰减已经成为影响桥梁结构使用寿命、严重威胁桥梁结构服役安全的最主要因素之一。将斜拉桥中斜拉索的病害进行治理,对避免重大安全事故的发生及减少全寿命周期内桥梁的总成本具有重要的科学意义和工程意义。
[关键词] 斜拉索; 病害;构成
[Abstract]: Cable-stayed bridge has large spanning capacity, simple structure type, the force is clear, aerodynamic stability, lightweight structure, aesthetic advantages, but the cable corrosion degradation and attenuation of fatigue resistance has e one of the most important factor for a bridge structure service life, a serious threat to the bridge structure serving the safety. Cable-stayed bridge in the diseases control, to avoid the occurrence of major accidents and to reduce the bridge across the life cycle cost has important scientific significance and engineering significance. [Key words: cable-stayed; disease; constitute
中图分类号::A文章编号:
斜拉桥是一种由索、塔、梁三种基本结构组成的复杂结构体系,具有自重轻,跨越能力强,施工便捷,墩台少,防洪、通航性能好;刚度大、伸缩缝少,行车平顺舒适;抗风能力强;造型美观、雄伟、挺拔等优点,是跨越大江大河的首选桥型之一,迄今为止,我国己建成各类斜拉桥一百余座。拉索是斜拉桥上的主要承力构件,担负着将主梁荷载传递到桥塔上的任务。由于拉索结构十分纤细,这使其成为斜拉桥结构体系中对病害最敏感的构件。在迄今发现的斜拉桥病害中,出现在拉索的病害占了绝大部分。这些病害导致拉索力学性能退化,耐久性降低。
一、斜拉索的损伤
斜拉索损伤主要有腐蚀损伤以及疲劳性能损伤:
1、腐蚀损伤
拉索的腐蚀主要是由于钢索与周围介质发生电化学作用,造成氧化还原反应所致。在拉索钢材中的合金元素、渗碳体及其它杂质往往构成阴极,铁元素构成阳极,当拉索表面凝结和吸附水汽而形成水膜时,就构成无数微电池,拉索就会被腐蚀。空气中的氧、二氧化硫、二氧化碳及氯离子等还会不断地溶解到水膜中去,促进铁元素的电离,加快钢索腐蚀速度。类似金属腐蚀,斜拉索腐蚀形态可分为两大类,即全面腐蚀和局部腐蚀。全面腐蚀常称为均匀腐蚀;局部腐蚀可分为点蚀、磨损腐蚀、应力腐蚀和腐蚀疲劳等。