TWIP钢在NaCl溶液中的腐蚀行为
刘向海、刘薇、刘嘉斌、舒康颖
材料科学与工程学院中国计量学院杭州310008 中国
摘要:采用电化学技术测定不同奥氏体含量的Fe-24Mn-- %NaCl溶液中的耐腐蚀能力,观察浸泡不同时长的表面腐蚀形貌,并分析其腐蚀机制。结果表明:%NaCl溶液中耐腐蚀性较差,第二相马氏体的出现会明显损害其耐腐蚀能力。TWIP钢的腐蚀行为可分为三个阶段:点蚀主导期、点蚀-均匀腐蚀过渡期、均匀腐蚀主导期。
关键词:TWIP钢;电化学;腐蚀形貌;腐蚀机制
CORROSION PROCESSES OF TWIP STEELS IN NaCl SOLUTIONS
LIU Xiang-hai,LIU Wei,LIU Jia-bin,SHU Kang-ying
College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, China
Abstract: The corrosion processes of Fe-24Mn-- TWIP steel in % NaCl neutral solution were studied with electrochemistry technique. The morphologies of tested steels with the different immersion times were observed, and the evolution features of corrosion were analyzed. The results showed that TWIP steel has low corrosion resistance and the whole corrosion process of TWIP steels can be divided into three segments: pitting corrosion-dominated stage, pitting and general corrosion stage and general corrosion-dominated stage.
Key words: TWIP steel; Electrochemistry; Corrosion surface; Corrosion mechanism
孪晶诱发塑性钢(TWIP钢)因具有优异的强韧性、高应变硬化性和高能量吸收能力等优点[1],成为汽车用高强韧钢板研究的热点之一。国内外学者初步确定了以Fe-(15~25)Mn为主体成分,选择性地添加一定量的Si、Al、C、Nb、N等合金元素的TWIP钢作为实验室研究和工业化生产的主要对象。同时,对TWIP钢的形变机制、显微组织和力学性能等方面都做了大量的研究[2-5]。
据统计[6],仅美国每年因汽车腐蚀带来的直接经济损失高达200亿美元以上。TWIP钢作为汽车用钢板,其耐腐蚀性也是值得关注的。Kannan等[7]对比了TWIP钢和IF钢在H2