近年来,灌浆材料在堵漏止水、帷幕防渗、基础加固和裂缝修补等方面的应用越来越广泛。其中水泥基灌浆材料是最受欢迎的,因为水泥基灌浆料加水拌合后具有流动性好、微膨胀、早期和后期强度高、不泌水等性能。
高强水泥基灌浆材料指由胶结料、细集料、水以及为实现某种功能而加入的外加剂或掺加料,按一定比例配制而成的,搅拌后浇注时无需振捣靠自重便可自由流变,达到要求均匀密实状态的结构用的灌浆材料。
本文采用试验研究的方法,通过改变砂胶比、水胶比以及外加剂和矿物掺合料等来测定水泥基灌浆材料的工作性能和力学性能,分析确定出影响水泥基灌浆材料性能的主要因素以及各因素的影响规律和最佳取值范围,最终优化出28d普通硅酸盐水泥基灌浆料抗压强度大于70Mpa的配合比。
关键词:水泥基灌浆材料;加固;流动性;抗压强度;配合比
ABSTRACT
In recent years, the grouting materials have been used more and more widely in water blocking, anti-seepage curtain, reinforcing in the foundation and repairing cracks. Cement-based grouting material is most ed for it mixed with water has some characteristics of good fluidity, micro-expansibility, high early and later strength and no bleeding.
High strength cementations’ grout is made up of binders, fine aggregate, water as well as some chemical or mineral admixtures with proper proportion. When placing, the mixture can flow freely to reach uniform pact state without vibrating.
This paper measured the workability and mechanical properties of cementations’ grout by changing sand -to- binder ratio, water-to-binder ratio and chemical or mineral admixtures, and analyzed every factor’s affect on the performance of cementations’ grout and their optimal value range ,consequently determined the main factors. Finally, the optimal mix of grout at 28d with pressive strength more than70Mpa was determined.
Key words: cementations’ grout; strengthening, fluidity, compressive strength, mix ratio
目录
摘要 I
ABSTRACT II
1 前言 1
灌浆料的发展历程 2
灌浆料的分类 3
国内外研究现状 5
水泥基灌浆材料性能要求 7
当前存在的问题 8
2 试验材料与方法 11
11
实验材料选择依据 11
试验所用原材料 13
实验方法 15
实验研究手段 15
实验仪器与设备 15
3 实验研究与结果分析 17
研究目的与研究内容 17
研究目的 17
研究内容 17
相关因素试验分析 18
高强水泥基灌浆材料配制 23
补充相容性试验 23
配合比确定 24
物理性能实验 25
本试验研究不足之处 26
结论 27
参考文献 28
致谢 30
前言
历史上,建筑业的发展大体经历了三阶段:即从大规模新建阶段,新建与维修并举阶段,到重点转向旧建筑物的维修、改造和加固阶段[1]。
在世界新兴经济体,随着经济建设的快速发展,它们的城市建设和水利、交通、房建等基础设施建