文档介绍：H08 H10焊条钢的冶炼工艺研究
089014112
(冶金与资源学院冶081班)
摘要:介绍日照第一炼钢厂H08A 焊条钢和青钢H10Mn2、H10MnSi焊条钢的冶炼工艺:H08A焊条钢在炼钢中转炉、连铸工序的过程控制及生产情况;采用氧气顶吹转炉冶炼、钢包底吹氩、小方坯连铸机和无扭控轧控冷高速线材轧机工艺生产H10Mn2、H10MnSi焊条钢。
关键词:H08A钢;H10Mn2钢;H10MnSi钢;冶炼工艺
The welding steel smelting technology research of H08 H10
089014112 FanBo
(College of metallurgy and resources metallurgy081)
Abstract: Introduce the first H08A steel welding steel and green steel H10Mn2, H10MnSi welding steel smelting process: the H08A welding steel in steelmaking converter, the process of continuous casting process control and production process; The oxygen furnace (smelting, ladle bottom blowing argon, small billet concaster and no twist controlled rolling accused of cold high-speed wire mill production process H10Mn2, H10MnSi welding steel.
Key words: H08A steel; H10Mn2 steel; H10MnSi steel; Smelting process
H08A 是典型的低碳低硅准沸腾钢, 该钢种由于含碳、硅低, 导致转炉出钢后, 钢水的氧含量偏高, 如果脱氧不充分, 高氧含量的钢水浇注后容易引起连铸坯产生气泡
, 高线轧制过程中易产生结疤、折叠等产品缺陷。使用含铝合金脱氧过低后易引起连铸浇注过程中絮流, 产生断浇, 另外温度控制, 吹氩控制、喂丝、保护浇注、保护渣等对铸坯的质量也有一定的影响。
1 工艺路线及技术措施
经过近三年的生产实践, 日照钢铁公司按照生产精品焊条钢的工艺原则, 逐渐制定出切实可行的冶炼工艺, 完善了钢水在线定氧、脱氧、吹氩搅拌、喂丝、大包保护浇注等技术措施, 以保证产品质量, 满足用户的使用要求。工艺路线如下:混铁炉铁水􀀂 60 t 转炉( 合金为Al􀀁Mn 铁、低碳锰铁) 􀀂炉后( 硅钙钡脱氧) 􀀂吹氩站( 定氧、Al􀀁Mn 铁脱氧、吹氩搅拌、定氧、喂丝、软吹) 􀀂连铸( 保护浇注、中包覆盖剂、专用保护渣) 。
2 成分与工艺控制
2. 1 Si 含量的控制
( 1) H08A 钢企业成分内控标准及用户要求标准见
( 2) Si 对焊条质量的危害。H08A 盘条是制造焊条的主要原料, 钢中Si 质量分数的高低直接影响焊条性能, 因此对Si 的质量分