粉末配比对毛细芯性能参数影响的实验研究.doc

文档介绍：中国工程热物理学会传热传质学
学术会议论文编号:123140
粉末配比对毛细芯性能参数影响的实验研究*资助项目:国家自然科学基金项目(No. 51106089)
辛公明,曲付龙,程林*
山东大学热科学与工程研究中心,济南 250061
(Tel:[phone],Email: ******@sdu.)
摘要本文以镍铜合金毛细芯为研究对象,通过烧结研制了一批不同粉末配比的毛细芯,分别测量计算了毛细芯的孔隙率和渗透率,分析了二者随铜粉比例的变化关系;同时采用稳态法测量了毛细芯的有效导热系数,着重研究了铜粉比例对毛细芯有效导热系数的影响。实验结果表明镍铜粉末配比为6:4时,毛细芯的有效导热系数获得最小值。
关键词环路热管,镍铜毛细芯,孔隙率,渗透率,有效导热系数
Investigation of ratio influences to the performances of Ni-posite wicks for LHPs
Gongming Xin, Fulong Qu, Lin Cheng*
Institute of Thermal Science and Technology, Shandong University, Jinan 250061, P R China
(Tel: [phone],Email: ******@sdu.)
Abstract: In this paper, a series posite wicks were sintered by using different ratio of nickel powders and copper powders. The influences of Ni-Cu ratio to the key parameters (including porosity, permeability and the effective thermal conductivity) of LHP wicks were experimentally measured and calculated. Results show that the addition of copper powders in the mixture can be helpful to the decrease of wick effective thermal conductivity, and the ratio 6:4 of Ni:Cu presented the minimum value in the tested range.
Keywords: loop heat pipe, Ni-Cu wick, porosity, permeability, effective thermal conductivity
0 前言
环路热管是一种高效的两相传热装置,利用蒸发器内多孔介质的毛细抽吸力驱动工质循环,通过工质的蒸发和冷凝传递热量,具有传热能力大、传递距离远、结构灵活等特点,目前已在空间热控制领域中得到了较广泛的应用[1-3]。同时环路热管在逆重力运行时的鲁棒性使其在地面电子设备应用领域具有良好的前景[4]。
毛细芯作为环路热管的关键部件,其孔隙率、渗透率、有效导热系数等参数对环