文档介绍：Co含量对玻璃光度指标的影响
摘要
熔制玻璃时加入少量玻璃着色剂,可制得各种有色玻璃。玻璃的着色不仅关系到各种颜色玻璃的生产,也是一种研究玻璃结构的手段。对着色玻璃,大家更关注玻璃的色度指标,但对玻璃的光度指标的影响因素相关研究不多。本文通过改变钴玻璃中钴含量、氧化还原剂用量、K2O用量来熔制玻璃样片,同时检验玻璃的热历史,然后用SP—1920 型分光光度计对玻璃样片进行光谱曲线的绘制分析。结果表明:着色剂用量、K2O的添加量及玻璃的热历史均对玻璃光谱曲线有较大影响,配合料的氧化还原气氛对该玻璃的光谱曲线影响不大。
关键词:钴玻璃,熔制,光度指标,光谱曲线
Cobalt content on the influence of glass photometric index
ABSTRACT
When a small amount of melting glass, glass coloring agents, can be obtained by a variety of colored glass. Colored glass of various colors of glass not only to the production, but also a means of discussing glass structure. Of colored glass, we are more concerned about the color index of glass, but the luminosity of glass studies factors Index few. By changing the cobalt glass cobalt oxide reducing agent, K2O content to melt glass samples, also examined the thermal history of glass, and then use SP-1920 spectrophotometer spectral curves of glass samples for analysis. The results showed that: the amount of coloring agent, K2O of addition and thermal history of glass were on the spectral curve of the glass have a greater impact, with the atmosphere of the redox material spectral curve of the glass has little effect.
KEY WORDS: cobalt glass,melting,brightness index,spectral curve
目录
前言 1
第1章实验 2
实验原料及所用设备 2
2
2
2
CoO用量实验 2
玻璃配合料氧化还原气氛熔制实验 3
热历史实验 3
K2O用量实验 3
第2章结果与讨论 5
5
氧化还原气氛对玻璃光谱曲线的影响 5
6
(K2O)含量不同对玻璃光谱曲线的影响 7
结论 9
谢辞 10
参考文献 11
附录 13
外文资料翻译 15
前言
玻璃对可见光的透过率是其主要的价值性能。颜色玻璃或带有某种“色调”的玻璃则多少不等而有选择性地影响透过率。玻璃着色后一般仍然保持透明,可是有些元素(Mn,Co)的着色能力很强,含有这些元素的玻璃,虽然浓度很低,厚度也很普通,已可能不透明。因此为了在生产过程中控制好色度指标的同时也更好的控制光度指标,该项目将系统的研究着色玻璃透光率的影响因素。希望能够提供一些光度指标的变化规律,减少生产的盲目性。本文通过改变着色剂含量、氧化还原剂用量、K2O用量以及热历史来熔制有色玻璃样片并用分光光度计对玻璃样片进行光谱曲线的绘制。然后对测得的光谱曲线进行分析,总结出这些因素对钴玻璃光度指标的影响规律,用于指导生产。
第1章实验
实验原料及所用设备
矿石原料包括硅砂、白云石、石灰石、长石、萤石五种;化工原料包括碳酸钠(Na2CO3)、硫酸钠(Na2SO4)、硝酸钠(NaNO3)、氧化钴(CoO)、氧化钾(K2O)[1]。
WAS50005电