摘要:前文报道了含不同含量丙烯酰胺的聚(N-异丙基丙烯酰胺-co-丙烯酰胺-co-3-丙烯酰
胺基苯硼酸)(P(NIPAM-AAm-AAPBA))微凝胶的合成极其温度敏感性。本文测定了其在不同
温度和 pH 条件下的葡萄糖敏感性,结果表明温度和 pH 值对微凝胶的葡萄糖敏感性具有很大
o
o
特别是 AAm 含量为 20%的微凝胶在此条件下显示了非常好的葡萄糖敏感性。在 50 mM 葡萄糖
存在下,其粒径增加倍,相当于体积增加倍。
关键词:微凝胶;温度敏感;葡萄糖敏感
中图分类号:O631
15
Glucose sensitive behavior of P(NIPAM-AAm-AAPBA)
microgel
SONG Wei, GUAN Ying, ZHANG Yongjun
(Key Laboratory of Functional Polymer Materials, Institute of Polymer Chemistry, College of
20
25
30
35
40
Chemistry, Nankai University, TianJin 300071)
Abstract: We have reported the synthesis and the thermosensitive behavior of a series of
poly(N-isopropylacrylamide-co-acrylamide-co-3'-acrylaminophenylboronic acid) (P(NIPAM-
AAm-AAPBA)) microgels with various AAm contents. Here their glucose-sensitivities at various
temperatures and pHs were measured. It was revealed that both temperature and pH influence the
glucose-sensitivity of the microgels. At and 25oC, the introduction of AAm monomer
increases the glucose-sensitivity of the microgel. At and 37oC, the introduction of AAm
monomer significantly increases the glucose-sensitivity of the microgel. Under these conditions,
the microgel with a AAm content of 20% exhibits excellent glucose sensitivity. In the presence of
50 mM glucose, a -fold increase in its diameter, corresponding to -fold increase in
volume, was observed.
Keywords: microgel; thermosensitive; glucose sensitive
0 引言
以苯基硼酸(phenylboronic acid, PBA) 为敏感基元的葡萄糖敏感水凝胶具有无毒、稳定
性好的优点。[1] 我们在前期工作中制备了以苯硼酸为葡萄糖敏感基元的葡萄糖敏感聚(N-
异丙基丙烯酰胺-co-3-丙烯酰胺基苯硼酸)(P(NIPAM-AAPBA))微凝胶[2,3],与相应的
宏观凝胶相比,其对葡萄糖的响应速度要快得多。[4] 这一新型材料已被应用于可自我调控
的胰岛素可控释放和葡萄糖传感器。[5,6] 然而此微凝胶还存在不能在生理条件下显示葡萄糖
敏感性的问题,因而大大限制了其应用。
为了解决这一问题,我们向其中引入第三单体丙烯酰胺,希望能提高其在生理条件下的
葡萄糖敏感性。前文报道了微凝胶的制备和温度敏感行为。本文测定了微凝胶在不同温度和
基金项目:科技部国际科技合作项目(基金号:2007DFA50760)及国家自然科学基金(基金号:20974050)
资助项目。
作者简介:宋微,(1987-),女,硕士研究生