浅层渗碳工艺控制.pdf

文档介绍：2
第 29卷第 5期热处理技术与装备 Vol. 29, No. 5
2008年 10月 RECHUL I J ISHU YU ZHUANGBE I Oct. , 2008
· 工艺·
浅层渗碳工艺控制
王平
(重庆重齿热处理有限责任公司技术工艺所,重庆 402263)
摘要:浅层渗碳由于速度快、时间短,因此渗碳过程控制难度较大,硬化层深度经常出现超差或者
表面硬度不符合技术要求,零件质量不理想。为此,我们利用 25 kW 井式渗碳炉对浅层渗碳的工艺
进行试验,找出了较好的渗碳工艺和控制方法,提高了零件渗碳淬火质量。
关键词:渗碳;浅层;工艺
中图分类号: TG156. 8 + 1 文献标识码: B 文章编号: 1673 - 4971 (2008) 05 - 0068 - 03
L ow - deep Carbur iz ing Process Con trol
WANG Ping
( Technical Process Department of Chongqing Gearbox heat treatment Co. , L td. , Chongqing 402263, China)
Abstract: Fast carburizing speed and short time are general features of low - deep carburization. In normal
carburizing and hardening p rocess, it is difficulty in p rocess control, and case dep th is often out of standard
or surface hardness is not p liance with technical specification and result in poor quality. Conse
quently, we perform low - deep carburizing p rocess control testing by using 25 kW well - type carburizing
furnace to imp rove carburizing and hardening quality.
Key words: carburizing; low - deep; p rocess
目前,我国对渗碳工艺过程的控制有了很大的产品零件。优化的渗碳工艺已广泛应用于 Mn =8. 0 mm
提高,特别是井式渗碳炉用于单件、小批件渗碳生产以下的齿轮类零件的渗碳淬火。
得到了大量的推广应用,一些不适合于采用多用炉
渗碳的零件也采用井式炉渗碳淬火。对于要求渗碳 1 浅层渗碳的工艺特性
层深度大于 1. 0 mm的零件在井式炉中渗碳,其工艺 1. 1 渗碳时间短
成熟,过程控制较容易;对于层深小于 1. 0 mm 的渗渗碳层深度要求取决于零件的工作条件及心部
碳控制就比较困难,尤其是井式炉滴注式气体渗碳, 强度。资料表明,齿轮零件硬化层深度一般根据齿
层深控制、表层碳浓度控制等相对于深层渗碳控制轮模数来确定,即 DC = ( 0