PAA添加量对PVC/PAA复合材料的影响
PAA添加量对PVC/PAA复合材料的影响
摘要:本论文以PVC/PAA复合材料为研究对象,通过共混改性方法,改性聚氯乙烯。首先使用两步法制备出合适分子量的聚酰胺酸, 通过热重分析、力学实验、红外光谱分析、偏光显微镜分析等手段,测试加入不同添加量的聚酰胺酸的复合材料的性能,从而分析探讨不同添加量的PAA对复合材料性能的影响。实验结果表明:随着PAA添加量的增加,PVC/PAA复合材料的拉伸强度、冲击强度以及断裂伸长率都呈上升的趋势,热稳定性也会提高。
关键词:复合材料,共混改性,聚氯乙烯,聚酰胺酸,添加量
Effect of PAA content on PVC/posites
Abstract: It is the research object about PVC/posite material in this paper, To modified Polyvinyl chloride (PVC) through blending modification methods. Two-step method to prepare different molecular weight of PAA by thermo-gravimetric analysis, mechanical test, Infrared spectrum analysis, polarizing microscope analysis methods, such as test to join different addition amount of polyamide posite materials performance, so as to analyze different addition amount of PAA on the properties posite materials. The experimental results show that: with PAA, with the increase of adding amount of PVC/posite materials tensile strength, impact strength and elongation at break are rising trend, thermal stability will also increase.
Keywords: composite material, blending modification, polyvinyl chloride, polyamide acid, adding quantity
目录
1 前言 2
聚氯乙烯 2
聚酰胺酸 2
研究目的及重要意义 2
论文研究内容 2
2 实验部分 2
实验原料 2
原材料 2
聚酰胺酸的合成 2
2
实验仪器及设备 2
实验工艺流程 2
聚酰胺酸分子量的测定 2
复合材料的制备 2
复合材料的成型及样品的制备 2
实验项目 2
冲击实验 2
拉力实验测试 2
热重实验 2
扫描电镜 2
偏光显微镜 2
红外光谱 2
垂直燃烧 2
3 结果与讨论 2
复合材料的力学性能分析 2
复合材料的热稳定性能的数据及分析 2
热重实验分析 2
垂直燃烧测试分析 2
复合材料聚集态结构及反应的分析 2
偏光显微镜图的分析 2
红外光谱图的分析 2
4 结论 2
参考文献 2
致谢 2
1 前言
聚氯乙烯
聚氯乙烯(PVC)是世界五大通用塑料之一,广泛应用于建筑,轻工业品,电线电缆,医药和农业等国民经济许多领域。PVC为无定形结构的白色粉末,支化度较小,具有价格便宜、透明性好、难燃、电绝缘性好和耐腐蚀等优点,可通过添加各种添加剂和运用多种成型方法制得性能各异、用途广泛的软质或硬质制品[1]。
工业生产的PVC分子量一般在5万~12万范围内,具有较大的多分散性,分子量随聚合温度的降低而增加;无固定熔点,80~8 5℃开始软化,130℃变为粘弹态,160~180℃开始转变为粘流态;有较好的机械性能,抗张强度60MPa左右,冲击强度5~10kJ/m2;有优异的介电性能。但对光和热的稳定性差,在100℃以上或经长时间阳光曝晒,就会分解而