文档介绍：唐山学院
毕业设计
设计题目:反应条件对水热法制备ZnWO4粉体的影响研究
系别: 环境与化学工程系
班级: 09无机非金属材料(2)班
反应条件对水热法制备ZnWO4粉体的影响研究
摘要
以二水钨酸钠和六水硝酸锌为原料,采用温和水热法制备了钨酸锌(ZnWO4)纳米粉体。采用X射线衍射(XRD)对其物相进行了测定。对其光催化性能进行了分析,着重研究了不同的反应条件对ZnWO4粉体的形貌的影响。探讨了ZnWO4粉体的最佳反应条件为:反应时间10h,反应温度190℃,反应的pH值为7。
关键词: 钨酸锌水热法反应条件光催化性能
The Research of Reaction conditions on the hydrothermal ZnWO4 Powders
Abstract
Put sodium tungstate dihydrate and zinc nitrate hexahydrate as raw material, the mild hydrothermal method was used to prepare zinc tungstate (ZnWO4) nanopowder. X-ray diffraction (XRD) of its phase were determined. And its photocatalytic performance was analysised, focusing on a different reaction conditions on the morphology of the powder ZnWO4. We conclude the optimal reactions of ZnWO4 powder were: reaction time was 10h, the reaction temperature was 190℃, the reaction pH was 7.
Key words: Zinc tungstate hydrotheal reactiormn conditions photocatalytic properties
目录
1 引言 8
9
9
10
11
12
13
光催化作用简介 13
14
16
17
17
17
18
ZnWO4粉体 20
ZnWO4简介 20
ZnWO4的制备现状 21
ZnWO4的光催化性能 22
2 实验 23
23
23
24
24
24
24
25
3结果分析与讨论 26
26
29
pH对产物形貌及性能的影响 30
4结论 32
谢辞 33
参考文献 34
1 引言
纳米材料是指材料的基本结构单元至少有一维处于纳米尺度范围(一般在1-100nm)。因其具有特殊的结构和性质,可以广泛地应用在物理、化学、光学、电子学等领域。金属钨酸盐的纳米粉体是一类重要的无机材料,在闪烁材料、光导纤维、光致发光物质、微波应用、湿度传感器、磁性器件、催化剂和缓蚀剂等方面具有良好的应用前景。特别是其光催化性能,为降解有机污染物(甲醛、罗丹明B和孔雀绿)及分解水开辟了一条新的途径,成为近几年重点研究的无机材料之一。[1]
目前已用提拉法、烧结法、固相复分解反应、溶胶-凝胶法、共沉淀法、水热法等制备出纳米级粉状的ZnWO4,其中水热法具有合成条件温和、结晶性能好、粒径分布窄等优点,是合成纳米材料理想的方法之一。[2]
本研究以Na2WO4·2H2O和Zn(NO3)2·6H2O为原料,采用水热法制备了ZnWO4催化剂,通过控制溶液的pH值、反应温度、时间等,制备了不同形貌的ZnWO4光催化剂,利用罗丹明B为目标降解物,探讨了ZnWO4的光催化性能。
水热法是在19世纪中叶地质学家通过模拟自然界成矿作用而进行研究的。科学家们是于1900年以后才创建了水热合成理论,并在以后的研究中向功能材料发展