文档介绍：无砂混凝土强度研究
王玲玲 1, 陈彦文 1, 徐长伟 1,史顺才 2
(1 沈阳建筑大学材料科学与工程学院,辽宁沈阳,110168
2 北京城建亚泰建设工程有限公司北京)
摘要:采用正交试验设计对无砂混凝土强度的影响因素及其发展规律进行分析。实验结果表明:集灰比和
集料粒级两个因素对无砂混凝土强度的影响相对显著。无砂混凝土的强度随着孔隙率的增大而降低,
随着龄期的增长而提高。
关键词:无砂混凝土;强度;正交试验;集灰比;龄期
Study on Strength of No-fines Concrete
WangLingling, Chen Yanwen,Xu Changwei Shi Shuncai
(1、Institute of Materials Science and Engineering, Shenyang Jianzhu University,
Shenyang, Liaoning, 110168 2、Beijing Urban Construction YataiEngineering
Co.,Ltd. Beijing , 100013)
Abstract: This paper adopts orthogonal experiment design to analyze the influential factors and
improving laws about the strength of no-fines concrete. Results show that aggregate cement ratio
and aggregate gradation are the relatively significant factors. In addition, the strength of no-fines
concrete decreases with its porosity increases, but improves with its age.
Key words: no-fines concrete; strength; orthogonal experiment; aggregate cement ratio; age
1 引言
无砂混凝土是由粗集料、水泥和水拌制而成的一种多孔混凝土。因其不含细集料,由粗
集料表面包覆一薄层水泥浆相互粘结而形成蜂窝状结构,具有一定的强度和渗透性,同时具
有轻质、吸声、环保等特点,是一种集承重、透水、反滤等用途为一体的新型工程材料[1]。
但是,无砂混凝土与普通混凝土相比强度较低,在很大程度上限制了其在工程中的应用。
本文深入全面研究无砂混凝土的强度发展规律及其相关影响因素,对无砂混凝土将来的发展
可以说具有重要的理论指导价值。
2 试验原材料
水泥
采用本溪工源水泥厂生产的工源牌矿渣硅酸盐水泥 P·。其性质如表 1 所示。
表1 水泥的性质
细度筛余凝结时间 3d强度/MPa 28d强度/MPa
安定性
% 初凝时间终凝时间抗折抗压抗折抗压
140min 220min 合格
集料
采用石灰岩碎石,筛分为 5mm~16mm、10mm~20mm 和 16mm~25mm 三种单粒级。筛
分过程中注意控制针片状颗粒含量。其主要质量指标见表 2,主要物理性能见表 3。
收稿日期:2010-08-05
表2 碎石主要质量指标
集料粒级/mm 压碎值/% 泥含量/% 泥块含量/%
5~16
10~20
16~25 0
表3 碎石的物理性能
项目 5mm~16mm 10mm~20mm 16mm~25mm
表观密度/(g·cm-3)
堆积密度/(kg·m-3) 1530 1453 1107
空隙率/%
吸水率/%
3 无砂混凝土强度的影响因素分析
选择因素水平
4
本文采用 L9(3 )正交表进行实验,其因素水平选择如表 4 所示。
表4 因素水平表
因素 A B C
水平水灰比集灰比集料粒级/mm
1 6 5~16
2 7 10~20
3 8 16~25
无砂混凝土 7d、14d 强度正交试验结果与极差分析
无砂混凝土 7d、14d 强度正交试验结果与极差分析详见表 5。
表 5 无砂混凝土 7d、14d