文档介绍：DOI:. RESEARCH ******@,2,刘璐1,张普玉1*(,河南开封475004; ,河南驻马店463000摘要:综述了有机硅改性苯丙乳液的机理、,重点阐述了化学改性法的最新研究进展,:有机硅;改性;苯丙乳液;研究进展中图分类号:O :A文章编号:1008-1011(201205-0097-06Research progress of styrene-acrylic emulsion anic siliconeCUI Yun-qi 1,2,LIU Lu1,ZHANG Pu-yu1*( of Fine Chemistry and Chemical Engineering,College of Chemistry and Chemical Engineering,Henan University,Kaifeng475004,Henan,China; of Chemistry,Huanghuai University,Zhumadian463000,Henan,ChinaAbstract:A review is provided of the recent research progress about the mechanism,modifica-tion methods and polymerization techniques of styrene-acrylic emulsion modified mixing method and chemical modification method are introduced,and thelatest advance in the chemical modification methods is ,suggestions arealso given about the development trend of styrene-acrylic emulsion modified anic sili- silicon;modification;styrene-acrylic emulsion;research progress 苯丙乳液是苯乙烯和丙烯酸酯类单体的共聚物乳液,其在国际上的发展越来越快,特别是在美国、日本、欧盟,,80年代开始正式投入使用,经过几十年的发展,现已广泛应用于建筑、、耐氧化性和耐油性,但是其耐水性和耐候性较差,且易于形变,限制了它的应用[1].有机硅具有优异的耐高、低温,耐辐射性和突出的耐水性,用有机硅对苯丙乳液进行改性,可以明显提高其耐水性、耐候性和抗沾污性等;除此以外,有机硅改性苯丙乳液比硅丙乳液有着更高的性价比,进一步扩大了其作为建筑涂料、金属表面乳胶涂料、地面涂料、 有机硅改性苯丙乳液的机理有机硅聚合物中硅氧键键能高达425kJ/mol,远大于碳氧键键能(351kJ/mol和碳碳键键能(345kJ/mo1,而且硅氧键间存在着d…π键和p…π键,使其具有抗氧化和抗分解性能[2-3].除此以外,有机硅分子收稿日期:2012-04-:河南省科技厅科技攻关重点项目(:崔运启(1972-,女,讲师,主要从事功能高分子方面的研究.*-mail:******@henu..98 化学研究2012年体积大、表面张力小和内聚能密度低,使其具有优良的透气性、抗黏污性和疏水性[2].有机硅和苯丙树脂的极性相差很大,将两类聚合物结合在一起,,按照其改性方法, 物理共混法物理共混改性,又称为冷拼法,分为两种方法[3]:一是将有机硅氧烷单体作为偶联剂或改性助剂直接加入苯丙乳液中改性;二是将有机硅氧烷制备成有机硅乳液,:可以引入较多有机硅;缺点是:聚硅氧烷与苯丙共聚物的极性相差很大,两者不能形成化学键,导致乳液稳定