CdSe量子点的合成及光学性能的研究.doc

文档介绍：
CdSe 量子点的合成及光学性能的研究
师忠根,温运明,莫艳梅,唐渝**
(暨南大学化学系,广州 510632)
5
10
15
20
25
30
35
40
摘要:以 NaHSe, CdCl2 为前驱体在水相中原位制备了 CdSe 半导体量子点,并通过 XRD、
UV-vis、PL、TEM、IR 等对产物的形貌及光学性能等进行了表征。在 CdSe 量子点制备过
程中,随 Cd:Se 的摩尔比减小以及 pH 值的增大,CdSe 量子点的粒径逐渐增大,其荧光强
度则与结晶性和粒径都有关,在 Cd:Se=10:4 及 pH 为 时,量子点的结晶性好和粒径较小,
荧光强度大。
关键词:CdSe 量子点;水相原位合成;荧光性
中图分类号:
Synthesis and optical properties of CdSe QDs
SHI Zhonggen, WEN Yunming, MO Yanmei, TANG Yu
(Department of Chemistry, JiNan University, GuangZhou 510632)
Abstract: CdSe QDs were synthesized using NaHSe and CdCl2 as precursors. The products were
characterized on the morphology and optical properties by XRD, UV-vis, PL, TEM, IR. The
particle size of CdSe QDs increases with decreasing the mole ratio of Cd:Se and increasing pH
values in the process of synthesis. The strength of photoluminescence is about both crystallinity
and particle size. The high strengths of photoluminescence of CdSe QDs with good crystallinity
and small particle size appear at Cd:Se=10:4 and pH value of .
Keywords: CdSe QDs; in situ aqueous synthesis; fluorescence
0 引言
量子点(Quantum Dots,QDs),是粒径小于或接近激子玻尔半径的一类特殊纳米粒子,
由于具有特殊的光、电、磁、催化等性质[1,2], 在基础研究和技术应用领域受到人们的高度重
视。在II-VI族半导体纳米晶中,CdSe 量子点由于其在可见光范围内的可调发射而受到广泛
的关注[3],金属有机相法和水相合成是目前制备 CdSe 量子点比较常用的方法,通过有机相
虽然可以制备高质量的 CdSe 量子点,但由于实验操作复杂,成本高且制备的 CdSe 量子点
不溶于水,其应用受到很大限制。目前水相法多采用 Se 粉为硒源制备 NaHSe 或 Na2SeSO3