文档介绍：SME 2713 
Manufacturing Process
Sheet Metal Forming
Assoc Prof Zainal Abidin Ahmad
UTM, Skudai
Outline
1. Introduction
2. Important characteristics
3. Cutting Operations
4. Bending Operations
5. Drawing Operations
6. Other OOtiperations
1 September 2008 Prof Madya Zainal Abidin Ahmad 2
1
1. Introduction
• The development is much at a later date pared with 
forging, rolling or extrusion processes, a round 1850s.
• Sheets are wide ly used due to a few reasons – prodiiductivity, 
good surface finish, close tolerance, high strength and 
various shapes can be produced. For large quantities, 
economical mass production operations are available,  
• Sheet metal working defined
– Cutting and forming operations performed on relatively thin 
sheets of metal.  
– Thickness of sheet metal ranging from  mm to 6 mm. 
– Thickness of plate stock > 6mm. 
– Operations usually performed as cold working
1 September 2008 Prof Madya Zainal Abidin Ahmad 3
1. Introduction
• Sheet and plate metal parts for consumer and 
idindus tiltrial proddtucts are numerous, such as
– Automobiles and trucks
– Airplanes
– Farm and construction equipment
– Small and large appliances
– Office furniture
– Computers and office equipment
1 September 2008 Prof Madya Zainal Abidin Ahmad 4
2
1. Introduction
Historical note
• Sheet metal stamping was developed as a mass 
production techlhnology for production of bblicycles 
around 1890’s.  This technology played an important 
role in making the system of interchangeable parts 
economical
1 September 2008 Prof Madya Zainal Abidin Ahmad 5
1. Introduction
Steps in making Hub Steps in making Sprocket
1 September 2008 Prof Madya Zainal Abidin Ahmad 6
3
Introduction
Three major categories of sheet metal processes
1. Cutting
– Shearing to separate large sheets, or cut part 
perimeters or mak