文档介绍：Chinese Journal of Nonferrous MetalsMar. 2009文章编号:1004-0609(2009)03-0484-06 焊后热处理对高强铝合金搅拌摩擦焊接头的影响王希靖1, 2,孙桂苹1, 2,张杰1, 2,徐成1, 2,李树伟1, 2,牛勇1, 2(1. 兰州理工大学甘肃省有色金属新材料国家重点实验室,兰州 730050;2. 兰州理工大学材料科学与工程学院,兰州 730050) 摘要:对航空用厚5 mm的7075铝合金搅拌摩擦焊试样热处理前后的焊缝微观组织及性能进行研究。结果表明:当搅拌头旋转速度为600 r/min、焊接速度为60 mm/min时,接头抗拉强度达到381 MPa,%;焊核区由6~7 μm等轴晶组成;经热处理后接头抗拉强度达到415 MPa;硬度的最低处在前进侧热机影响区;断口的微观形貌具有强化相的韧窝特征,且断裂几乎发生在前进侧的热机影响区;7075铝合金搅拌摩擦焊接头的薄弱点在热机影响区。关键词:7075铝合金;搅拌摩擦焊;微观组织中图分类号:TG 453+.9; TG :A Effects of heat treatment after welding on friction stir welding joints of high-strength aluminum alloy WANG Xi-jing1, 2, SUN Gui-ping1, 2, ZHANG Jie1, 2, XU Cheng1, 2, LI Shu-wei1, 2, NIU Yong1, 2(1. State Key Laboratory of Advanced Non-ferrous Metal Materials, Gansu Province, Lanzhou University of Technology, Lanzhou 730050, China; 2. School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou 730050, China) Abstract: The microstructure and property before and after heat treatment of friction stir welded 5 mm aero 7075 aluminum alloy were investigated. The results show that when the rotating speed of stirring joint is 600 r/min and the welding speed is 60 mm/min, the tensile strength can reach 381 MPa that is % of the base metals, which are regarded as the most ideal parameters under experimental conditions. There are equiaxed grains with size of 6?7 μm in weld nugget. After heat treatment, the tensile strength can reach 415 MPa. The lowest hardness appears in thermomechanically affected zone (TMAZ) of advancing side. The fractography has a characteristic of dimples of strengthening phase and the strain fracture appears in TMAZ of advancing side of joints. The weak point of friction stir welding joint for 7075 aluminum alloy occurs in the TMAZ. Key words: 7075 aluminum alloy; friction stir welding; microstructure搅拌摩擦焊(FSW)是英国焊接研究所发明的一种固相连技术[1],自发明以来,在世界范围内引起了广泛的关注[2?5]。与传统工艺相比,搅拌摩擦焊具有连接温度低、焊后残余应力小、接头性能高等一系列优点[