文档介绍：LiBH4制备工艺的研究
摘要
本文通过气-固反应法研究了LiBH4的制备工艺。在试验中,研究了LiBO2•8H2O的干燥工艺;分析了球磨对LiBO2+Mg混合物反应的影响;同时还研究了温度和压力对球磨产物氢化时的影响。从结果中发现,LiBO2•8H2O最佳干燥工艺为:先在170 ℃时干燥2小时,然后在650 ℃下干燥3小时。LiBO2+Mg在氢气气氛下球磨50小时后的产物为MgH2+非晶相LiBO2,同时还剩有部分未反应的Mg。在氢气气氛下球磨50小时后的产物经200~290 ℃氢化处理(氢气压力5 MPa)24小时后的产物比较复杂,但并不能得到LiBH4。但该球磨产物在250 ℃、7 MPa下氢化处理36小时后可以得到LiBH4。
关键词:氢化物合成晶体结构
Study on preparation process of LiBH4
Abstract
LiBH4 was prepared essfully by Gas-Solid reaction of LiBO2+Mg+H2 in this work. The drying process of LiBO2•8H2O was investigated at first. The effects of ball milling on the reaction of the LiBO2+Mg mixture were then analyzed. Finally, the effects of hydrogenation pressure and temperature on the reaction products were studied. It was found that the optimal drying process of LiBO2•8H2O was drying at 170 ℃ for 2 hours firstly and then drying at 650 ℃ for 3 hours. The ball milling products were MgH2 and the amorphous LiBO2 when the LiBO2+Mg mixture was milled for 50 hours under hydrogen atmosphere. However, a small amount of unreacted Mg existed after ball milling. The products plicated when the ball milled product was hydrogenated at 200~290 ℃ for 24 hours under a hydrogen pressure of 5 MPa. However, LiBH4 can be obtained by the hydrogenation of the ball milled product at 250 ℃ for 36 hours under a hydrogen pressure of 7 MPa.
Key Words:Hydride Synthesis Crystal structure
毕业设计(论文)原创性声明和使用授权说明
原创性声明
本人郑重承诺:所呈交的毕业设计(论文),是我个人在指导教师的指导下进行的研究工作及取得的成果。尽我所知,除文中特别加以标注和致谢的地方外,不包含其他人或组织已经发表或公布过的研究成果,也不包含我为获得及其它教育机构的学位或学历而使用过的材料。对本研究提供过帮助和做出过贡献的个人或集体,均已在文中作了明确的说明并表示了谢意。
作者签名: 日期:
指导教师签名: 日期:
使用授权说明
本人完全了解大学关于收集、保存、使用毕业设计(论文)的规定,即:按照学校要求提交毕业设计(论文)的印刷本和电子版本;学校有权保存毕业设计(论文)的印刷本和电子版,并提供目录检索与阅览服务;学校可以采用影印、缩印、数字化或其它复制手段保存论文;在不以赢利为目的前提下,学校可以公布论文的部分或全部内容。
作者签名: 日期:
目录
引言 1
1. 文献综述 2
氢能源 2
氢能源的储存材料----金属氢化物 2
硼氢化物的结构、性质和应用 4
硼氢化物的结构 4
硼氢化物的物理化学性质 5
硼氢化物的应用及水解制氢 6
硼氢化物的合成方法 8
硼氢化锂的制备 8
其他硼氢化物(硼氢化钠)的制备 10
本文的目的意