文档介绍：摘要
论述了Mg-Al-Zn系合金经过固溶处理后组织和耐腐蚀性能的变化。通过观察经固溶处理后的组织及塔菲尔曲线,对Mg-Al-Zn系合金固溶处理后的组织和电化学腐蚀行为进行了研究。结果表明,经过固溶处理后的镁合金显微组织晶粒长大明显,β-(Mg17Al12)相部分溶解在基体组织中,在温度达到560度以上时,组织发生过烧现象。与未经处理镁合金的耐腐蚀性能相比,经过固溶处理后的镁合金耐腐蚀性能无明显增加。
关键词:镁合金;固溶处理;显微组织;耐腐蚀性能
Title: Solution Treatment on Mg-Al-Zn anizations and the impact of corrosion resistance
Abstract
Discusses the Mg-Al-Zn alloy after solution treatment and corrosion resistance after anization changes. By observing anization after solution treatment and the Tafel curves of Mg-Al-Zn alloy after solution treatment and electrochemical corrosion behavior was studied. The results showed that, after the magnesium alloy after solution treatment microstructure grain growth significantly, β-(Mg17Al12) phase partially dissolved in the anization, in the temperature reaches 560 degrees, the tissue over-burning phenomenon. With untreated corrosion resistance of magnesium pared to that after the magnesium alloy after solution treatment did not increase the corrosion resistance.
Keywords: Magnesium alloy;Microstructure;Corrosion resistance
毕业设计(论文)原创性声明和使用授权说明
原创性声明
本人郑重承诺:所呈交的毕业设计(论文),是我个人在指导教师的指导下进行的研究工作及取得的成果。尽我所知,除文中特别加以标注和致谢的地方外,不包含其他人或组织已经发表或公布过的研究成果,也不包含我为获得及其它教育机构的学位或学历而使用过的材料。对本研究提供过帮助和做出过贡献的个人或集体,均已在文中作了明确的说明并表示了谢意。
作者签名: 日期:
指导教师签名: 日期:
使用授权说明
本人完全了解大学关于收集、保存、使用毕业设计(论文)的规定,即:按照学校要求提交毕业设计(论文)的印刷本和电子版本;学校有权保存毕业设计(论文)的印刷本和电子版,并提供目录检索与阅览服务;学校可以采用影印、缩印、数字化或其它复制手段保存论文;在不以赢利为目的前提下,学校可以公布论文的部分或全部内容。
作者签名: 日期:
目录
目录 3
第一章绪论 4
选题的目的与意义 4
镁合金 5
镁合金的发展 5
镁合金的性能及应用 6
镁合金在汽车上的应用: 6
镁合金在3C产品上的应用: 7
镁合金的种类及发展趋势 7
镁合金的种类 7
镁合金的发展趋势 8
合金元素对镁合金组织和力学性能的影响 10
镁合金主要化学成分 10
合金元素对合金组织和力学性能的影响 11
固溶处理的作用 13
固溶与时效处理 13
稀土镁合金 14
稀土镁合金的发展现状 14
稀土镁合金的开发应用及前景 15
本论文的主要研究内容 16
第二章试验方法及设备 17
实验选用材料 17
固溶处理实验所使用的材料 17
金相实验选用的材料 17
耐腐蚀实验所使用的材料 17
X射线衍射实验所使用的材料 17
实验方案 17
实验过程