文档介绍：铝及铝合金化学浸镀仿金工艺研究
摘 要：为了拓展铝及铝合金的应用范围，采用二次浸锌+碱性化学镀鎳+酸性化学镀鎳+ 化学浸镀仿金组合工艺的方法研究一种新的铝及铝合金化学浸镀仿金工艺。其工艺规范 如下：硫酸亚锡llg/L,磁铜1. 3g/L,勰（98%） 20mL/L,酒S酸9g/L,藜酸45mL7L, ,稳定剂XL-97B 10mL/L,温度：常温，时间5-10min。探讨了主要成分 和工艺条件对仿金镀层质量的影响。采用目测法、弯曲法、耐盐水腐蚀实验检测了仿金 镀层的外观、结合力和耐蚀性。检测了仿金镀层在5%NaCl溶液中的电化学参数，结果 表明：所形成的仿金层色泽典雅纯正，达18-22K,结合力好，耐蚀性好，且镀液成分简 单，操作简单，对环境污染小，因而具有良好的应用前景。
关键词：铝及铝合金；化学浸镀；仿金；性能检测
Immersion plating of copper-tin alloy on Aluminum Alloys
Abstract: In order to expand the Aluminum Alloys application fields,a new immersion plating process was developed with “zincate solution two times+alkaline electroless nickel+acid electroless nickel+immersion plating^.The basic formula was studied:stannous sulfate 1 lg/L,copper sulfate ,sulphuric acid 98% 20mL/L,tartaic acid 9g/L,hydrofluoric acid 45mL/L,ammonium fluoride ,stabilizer to tin salt XL-97B 10mL/L,in normal temperature,controlling the time in 5- main components and plating solution were studied that influence the quality of coating performance. Adopting eye-measurement,bendingmethod,saline resistant performance tested the properties of Cu-Sn coating appearance,adhesion,corrosion the electrochemical parameter by CHI660B electrochemical show that the immersion plating Cu-Sn coating has better quality,purity eleqance,which can reached 18-22K,it has good bending force,high corrosion resistance and the process condition and operation are simplence ,lower pollution to process has a widely untilization in field.
Key words: Alumium alloy;immersion plating;gold imitation;performance testing.
1前言
众所周知，金是一种具有高光泽度、呈金黄色、色泽瑰丽夺目、化学性子稳定的贵 金属。金黄色的外观华丽贵重，一直都被视为财富的象征而备受人们的青睐。但金价昂 贵，用于装饰极不现实。而仿金镀则调节了价格与装饰要求的矛盾，故而很多制品都采 用装饰性仿金镀，同样给人以高雅的感觉。目前在金属制品上获得金色表面装饰层的方 法很多，主要方法有①真空镀膜法；②彩色电泳法；③纯金电镀法；④浸渍镀仿金法； ⑤仿金电镀法。其中，仿金电镀成本低且镀层可接近纯金镀层的装饰效果，因而得到了 广泛的应用。氧化仿金电镀工艺成熟，具有镀液稳定、镀层色泽容易控制、外观装饰性 好等优点，但镀液有剧毒，对环境污染严重，因而无氧镀仿金电镀成了电镀研究的热点。 近年来发展的仿金电镀体系有焦磷酸盐、柠檬酸盐、酒石酸盐和HETP,得到了一定的应 用。为了得到色泽