文档介绍：第二甚全|有色盒■分析检—s标准化技水交流研讨会会秘锌铝合金时效后硬度低原因分析江河,杨振英(深圳市美信检测技术股份有限公司,深圳宝安518108) 【摘要】针对某新型锌铝合金时效处理后硬度低问题,经来料硬度检查、化学成分分析、金相检查、 SEM+EDS分析、材料热处理性能分析、热处理验证试验等方法,确认该合金是在ZA50型系列锌铝合金的基础上开发得到,并找出该新型合金的热处理规律,针对客户具体的硬度需求,提出改善措施。【关键词】锌铝合金;固溶处理;时效处理 Reason analysis tolowerhardness afterageing forZ-A alloy JIANG He,YANG ZHenying (MeixinTestingTechnology Co.,Ltd,BaoAn,ShenZhen,China,51 8108) Abstract:Counter lower hardness afterageing for a new Z-A alloy,analysis ing hardness checking, chemical element analysis,checking with a microscope,SEM+EDS analysis,heat treatment performance analysis,heat treatment evaluating test,etc.,it could beconfirmed thatthe new alloy isdeveloped as basis for the series Z—A alloytyped the meantime,the heat treatment rulewere found,and some improving method were suggested tomeet theveryhardness standard from the customer. Key words:Zinc—aIuminium alloy;solution treatment;ageing treatment 背景介绍某型锌铝合金是客户新开发的材料,用N型代替, 图1、图2分别为用N型锌铝合金材料制造的手机盖产品正反面。技术要求热处理后硬度145HV以上。送检前, 客户采用120~220。C区间的各种温度时效12小时试验,结果硬度都低于145HV,无法正常生产,需分析原因。图1样品正面图2样品背面 Fi备1 front surface缸the s枷ples back surface ofthe samples 一39. 2检查分析、后的产品切片检验硬度,热处理前的产品硬度检测结果为:147~,接近技术要求的下限值;经188。Cxl2h热处理后的产品硬度检测结果为:~,硬度下降,硬度值低于技术要求。 +ICP检查来样材料化学成分,结果见表1,主要成分为AI亿nlCulSilFe,没有检i贝wlNc 和S含量。与ZA50型锌铝合金元素含量【1】对比,确定 N型锌铝合金实际上属于乙A50型系列锌铝合金成分。表1 化学元素分析结果(W僦) Tablel chemi