文档介绍：摘要
焊条电孤焊是药皮焊条手工电孤焊的简称。是用手工操纵焊条进行焊接的电孤焊方法。由于焊条电孤焊设备简单、操作灵活、可焊金属材料广等特点。焊条电孤焊主要用于焊接装配要求不高、结构复杂的单件或小批量的产品。本课题为了研究球墨铸铁与Q2 process performance and use performance superior to that of structural steel electrode J422,Structural steel welding rod specimens used in the experimental process appearedobvious cracks, unable to reach the corresponding performance addition to the use of SMAW specimens in the process of welding, especially prone to inclusion of welding defects. At the same time, experiments have proved that the new material WE777 in the formation of weld and weld mechanical properties of cast iron electrode Z408 This proves that, in the welding of ductile cast iron and Q235 dissimilar metalmaterials in the process of using, in the premise of the same welding method,welding process the right welding material use and reasonable welding process, is essential.
Key words: Arc welding Nodular cast iron Q235 Metallographic organization
Welding defects
第一章绪论 1
1
2球墨铸铁 1
3碳素结构钢 2
3
. 1 Q235普通碳素结构钢焊接性分析 4
4
5
5焊接方法及焊接材料 6
9
9
第二章实验材料及实验方法 10
1实验材料 10
2实验方法 10
2. 1试件焊前准备 10
2. 2. 2球墨铸铁与Q235钢板施焊方法 11
2. 2. 3微观组织观察 12
2. 13
2. 2. 5接头硬度实验 13
第三章实验结果及分析 14
1碳钢焊条所焊试件开裂原因及分析 14
2焊缝成型观察 14
3焊接接头显微组织微观结构观察分析 15
20
21
第四章结论 23
谢辞 24
参考文献 25
第一章绪论

铸铁是一种以碳、铁、硅为主要成分且在结晶过程中具有共析转变的多元铁基合金。碳在铸铁中既可以以化合态的渗碳体（Fe’C）形式存在，也可以以游离状态的石墨（G）形式存在。根据碳在铸铁中的存在状态和形式不同，可以将铸铁分为五类［1］。
（1）白口铸铁。碳在铁中绝大部分以渗碳体（Fe’C）形式存在，因其断口成白色而得名。渗碳体的硬而脆、硬度为800HBSo因无法机械加工，所以应用不广，主要用于轧辐或其他不需要机械加工的耐磨零件。
（2）灰铸铁。碳以片状石墨存在，因其端口成灰色而得名。普通灰铸铁中石墨片状较粗，如果在浇注之前向铁水中加入少量硅铁或硅钙等孕育剂，进行孕育处理，促使石墨非自发形成形核，可以使灰铸铁粗片状石墨细化，形成孕育铸铁。
（3）可锻铸铁。碳以团絮状石墨存在。是将灰铸铁经过长时间的石墨化退火, 是渗碳体分解并析出石墨以团絮状分布在基体内。
（4）球墨铸铁。碳以球状石墨的形式存在，简称球铁。是在浇注前向铁水中加入纯镁或稀土镁合金等球化剂而获得。球铁具有较高的强度和韧性，还可以通过热处理显著地改善其力学性能，故常用来制作强度较高、形状复杂的铸件。
（5）蠕墨铸铁。碳以蠕虫状石墨存在。在浇注前向铁水中加入稀土硅铁、稀土镁钛等稀土合金的蠕化剂，促使石