文档介绍：钢结构低温焊接工艺
生产实****论文
学院:
专业: 学号: 姓名: 指导教师: 实****日期:
罗正才
(河海大学,土木与交通学院,江苏省南京市,210009)
摘要:钢结构低温焊接,钢材在焊接前后都有较大的温度变化,容易发生钢结构焊缝接头区出现冷裂纹现象。因此,在寒冷地区冬季施工焊接时保证钢结构中厚钢板低温焊接质量是最重要的一个环节。本文以沈阳恒隆市府广场为例,简略地阐述了钢结构在低温环境下的焊接工艺和技术措施。
关键词:低温焊接裂纹控制
中图分类号:TG457 文献标志码:A
Analysis of the steel structure low temperature welding process
Abstract: Steel low-temperature welding, steel before and after welding has larger temperature changes, cold cracking phenomenon prone steel weld joints. Therefore, ensure that the steel structure in the soldering quality is the most important aspect of the thick steel plate welding in cold regions. This paper briefly described the welded steel structure in a low temperature environment technology and technical measures .
Keywords: low-temperature welding crack control LUO Zhengcai (Hohai University, School of Civil Engineering and Transportation, Nanjing, Jiangsu Province, 210009)
0 引言
钢结构低温焊接对焊缝的危害直接表征就是出现裂纹和
在工作状态下发生脆断。为保证焊缝能够满足设计要求,采
用合理的低温焊接技术和工艺措施是保证工程质量合格的
关键。本文通过沈阳市府恒隆广场在冬季温度低达-30℃的
条件下焊接施工作业为例,浅析低温焊接中厚板工艺和技术
措施在建筑钢结构工程中的应用。
1 焊接工艺的选择
接头坡口形式:焊接接头开坡口主要是为了保证电弧能
深入焊缝根部,使根部能够焊透。在选择坡口形式时应考虑
保证焊缝焊透,坡口形状易加工,提高劳动效率,节省焊材,
减小焊后变形的可能性等。因此,实际工程中应根据现实条
件采用合理的坡口形式。本工程钢板主要采用单边坡口焊,
T形接头采用K形坡口。
焊接材料:钢结构焊接接头的质量在很大程度上取决于
所选用的焊接材料。焊接材料的选择必须根据母材的成分、
性能、接头形式及质量要求综合考虑。焊接材料选择不当,
熔敷金属中掺入合金元素,易使焊缝过渡区产生脆相或裂
纹。因此,在超低温条件下焊接,在满足设计强度的要求下,
优先