文档介绍：50CrVA 淬硬性偏低原因分析·1·
50CrVA 淬硬性偏低原因分析
罗贻正祝小冬
(方大特钢科技股份有限公司,江西南昌 330012)
摘要通过使用同批次原材料在相同工艺温度条件下,使用不同淬火介质做淬火实验对比,结合 GB/T 1222—2007
《弹簧钢》标准中规定的实验室条件下的淬火结果,分析了导致 50CrVA 弹簧钢淬硬性偏低的原因,从而确定导致
此批材料淬火后硬度偏低是由于淬火介质冷却能力不足所致。
关键词 50CrVA,淬火介质,硬度偏低
Analysis of the Low Hardness of 50CrVA
Luo Yizheng, Zhu Xiaodong
(Fangda Special Steel Technology Co., Ltd., Nanchang Jiangxi 330012, China)
Abstract By use the same batch of raw materials in the same process temperature conditions, adopt of different quenchant to
compare the result of quenching test, refer to the laboratory conditions quenching result of according to the GB/T 1222—2007
《Spring Steel》 standard, analysis of the reason which caused to 50CrVA spring steel has low hardenability, and determine the
reason of this batch of material from the lower hardness after quenching is due to inadequate cooling power of quenchants.
Key words 50CrVA, quenchant, low hardness
某公司曾购入一批 50CrVA 材质,100mm×32mm 规格的弹簧扁钢。该公司在进行淬火时发现,工件在
淬火后硬度在 HRC40~48 之间,远低于该公司要求不低于 HRC53 的标准。淬火工艺参数:加热区温度设
定 960℃,保温区温度设定 940℃,从入炉到出炉时间 67min,工件入淬火介质温度大于 870℃。该公司原来
使用的是 N32 机械油做淬火介质,出现此情况后改为某厂生产的 Y15D 型快速淬火油,淬火后工件硬度仍
然在 HRC40~50 之间。
1 实验
端淬实验
取现场同批次的原材料依照《钢的淬透性末端淬火实验方法》要求加工成标准试样,试样的热处理工艺:
860℃保温 30min 正火。860℃保温 25min 顶端淬火,水温 21℃,冷却 10min。端淬数据见表 1。端淬曲线见
图 1。
表 1 端淬数据
距端部:mm 3 6 9 12 15 18 21 24 27 30 33
硬度:HRC