文档介绍：影响低需水量水泥性能的几个因素
2008-10-10 作者:
 
摘要采用立窑水泥熟料、矿渣和石膏,掺加适量助磨减水外加剂,研制了新型低需水量水泥。研究了粉磨工艺、细度及S03含量对低需水量水泥性能的影响。结果表明,当采用混磨工艺,比表面积大于500m2/kg,%~%,矿渣掺量达40%时,仍可获得28d抗压强度高于50~60MPa的水泥,用这种水泥可直接配制C50~C60高流态混凝土。
Abstract The authors describe that shaft kiln clinker,slag,gypsum and suitable amount of grinding aid and water reducer as admixture has been adopted new to produce type low water requiring cement in this paper. The influence of grinding process,fineness and SO3 content on cement properties requiring low quantity of water has been show that pressive strength of cement is still higher than 50~60MPa,when specific surface area is higher than 500m2/kg SO3 content is %~% and adding rate of slag reaches40%,C50~C60 high fluidity concrete can be directly produced for using this kind of cement.
随着高性能混凝土日益广泛地应用于土木建筑工程,混凝土的配制变得日益复杂。现在配制高性能混凝土,除传统的水泥、砂、石和水以外,还需要各种外加剂、矿物掺和料等,原料种类可多达10种。这些新的原材料掺加量小,掺量要求精确控制,这样,使混凝土的配制工艺复杂,质量控制比较困难。另外水泥与高效减水剂的相容性问题也是高性能混凝土特有的问题。为解决上述问题,吴中伟教授提出应研制高性能混凝土专用胶凝材料〔1〕。俄罗斯已研制出了用于高强混凝土的新型低需水量水泥〔2〕。西班牙低水粘合剂公司在研制低需水量胶凝材料〔3〕。国内也开展了类似的研究工作〔4〕。本文采用立窑生产的硅酸盐水泥熟料,配制了低需水量水泥,研究了粉磨工艺、水泥细度及SO3含量对所研制的水泥性能的影响,并进行了混凝土试验。
1 试验所用原材料
采用河北香河水泥厂立窑生产的硅酸盐水泥熟料、首钢矿渣和太原石膏。原料的化学组成见表1。水泥熟料的矿物组成及物理性能见表2。
表1 原料的化学组成(%)
Loss
SiO2
Al2O3
Fe2O3
CaO
MgO
R2O
SO3
熟料
矿渣