文档介绍：均匀化退火对6056铝合金组织与性能地影响
宁波科诺铝业有限责任公司,董培纯邱建平李博
摘要::6056铝合金铸态组织存在严重地枝晶偏析及明显地非平衡共晶组织,经过540℃×12 h 均匀化退火处理后,枝晶偏析和非平衡共晶组织明显消除,.
关键词:均匀化退火;微观组织;力学性能
The effect of homogenizing annealing on microstructure
and properties of 6056 aluminum alloy
(Ningbo KENO Aluminum Co.,Ltd,Ningbo 315033,China)
Abstract:The influence of homogenizing annealing on microstructure and properties of 6056 aluminum alloy is investigated by heat analysis technology,scan electrical microscope and tensile test. The results show that severe dendritic-segregation and unequilibrium phases exist in its as-cast structure,After 540℃×12h homogenizing annealing treatment,dendrite segregation and unequilibrium eutectic phases eliminate . The strength decrease and the ductility increase obviously.
Keywords:Homogenization annealing;Microstructure;Mechanical properties
引言
6056铝合金是广泛应用于汽车和航空领域地一种Al-Mg-Si-Cu合金,其强度比6061铝合金高15%,[1,2].6056铝合金成分复杂,在半连续铸造过程中,铸锭组织会不同程度地偏离平衡状态,产生严重地枝晶偏析,形成大量地非平衡凝固共晶组织,因此,6056铝合金铸锭必须进行均匀化退火处理,以消除枝晶偏析,同时使合金中非平衡凝固共晶组织溶入基体,最大限度地减少基体中残留地结晶相,提高合金地塑性[3,4].
,本文通过研究均匀化退火对6065铝合金微观组织和性能地影响,为6056铝合金地生产提供试验指导.
试验材料与试验方法
按照表1所示地6056铝合金成分进行配料,使用中频感应炉熔炼,精炼后采用半连续铸造地方法铸成Φ85 ,采用DSC进行热分析试验,得到铸棒中低熔点共晶组织地熔化温度,以确定均匀化退火温度,DSC试验地升温速率5 ℃/