文档介绍：编号
本科生毕业论文
道路混凝土耐久性的研究
Study on durability and application of road high performance concrete
学生姓名
专业
无机非金属材料工程
学号
060612103
指导教师
学院
材料科学与工程
2010年6月
摘要
从耐磨性、干缩、抗裂性等方面,研究了粉煤灰、矿渣两种矿物掺合料对道路高性能混凝土性能的影响,并初步探讨了其影响机理。研究结果表明:掺人质量分数为20%一40%粉煤灰和矿渣的道路高性能混凝土具有工作性好、后期强度高、耐磨、低收缩以及抗裂性好等特点。工地应用表明,用粉煤灰与矿渣复合双掺配制的道路高。
关键词: 粉煤灰;矿渣;道路混凝土;耐久性;应用

Abstract:The efects of two minerals admixtures of fly ash and slag on road high performance concrete is studiod through the aspects of abmsion resistance,drying shrinkage,cracking resistance and so the same time,the mechanism of action was analyzed and research results showed that road high performance concrete added 20%--40% by mass of fly ash and slag have good workability,higher later strength,beaer characters of abrasion resistance,lower drying shrink age,anti-cracking and so results of application indicated that high performance concrete mixed with fly ash and slag can significantly improve the pavement performance.
Key Wrrds: fly ash;slag;road concrete;durability;application
摘要 I
第一章绪论 - 1 -
混凝土的应用与发展概述 - 1 -
高性能混凝土的技术特点及要求 - 1 -
高性能混凝土在国内外工程中实际的应用 - 1 -
高性能混凝土存在的问题以及今后的发展趋势 - 2 -
现代混凝土的特点 - 2 -
现代混凝土配合比设计方法 - 3 -
化学外加剂与胶凝材料的相容性 - 4 -
矿物掺合料的合理使用 - 4 -
其他特种材料的应用 - 5 -
混凝土强度浅析 - 6 -
第二章道路混凝土耐久性的实验性研究 - 10 -
原材料与试验方法 - 10 -
原材料 - 10 -
试验方法 - 11 -
试验结果及分析 - 11 -
力学性能 - 11 -
耐磨性能 - 11 -
干缩性能 - 12 -
抗裂性能 - 13 -
工程应用 - 14 -
结论 - 15 -
第三章当今混凝土耐久性的研究现状和研究方向 - 17 -
混凝土耐久性研究的背景 - 17 -
混凝土耐久性研究的意义 - 18 -
混凝土耐久性的研究动态 - 18 -
混凝土耐久性研究的现状和评述 - 19 -
材料耐久性研究 - 19 -
混凝土碳化研究 - 19 -
. 1. 2钢筋锈蚀研究 - 19 -
. 1. 3 冻融破坏研究 - 20 -
结构耐久性研究 - 20 -
. 2. 1 结构的耐久性评定 - 20 -
. 2. 2 结构构件寿命预测 - 21 -
. 2. 3 结构寿命预测 - 21 -
今后混凝土耐久性研究的方向 - 22 -
第四章提高混凝土耐久性若干措施 - 23 -
科学严谨地进行原材料的质量检验 - 23 -
降低混凝土的渗透性 - 24 -
改善混凝土的体积稳定性 - 25 -
4.