文档介绍：毕业论文中文摘要
本课题研究在ABS塑料基体上进行镍磷铜共沉积以获得一定厚度具有电磁屏蔽性的复合镀层。课题主要探究了复合镀的施镀温度、镀液pH及硫酸铜的加入量对镀层厚度、表面形貌等的影响,通过金相显微镜、SEM、XRD对镍磷铜复合镀层的微观形貌、镀层物相进行分析,结果表明:在镍磷镀基础镀液上,CuSO4 含量为4g/L、温度80℃,,获得的镀层胞状组织均匀细小与ABS基体结合力强并可以完全覆盖于基体表面,镀层的XRD分析显示在镍磷非晶态“馒头峰”上叠加着Cu合金的(200)、(220)等晶面的特征衍射峰,表明在ABS基体经优化的工艺与镀液配方下获得了镍磷铜共沉积复合镀层。并证实了镀层的形成与增长是胞球堆积生长的机制。
关键词 ABS基体镍磷铜复合镀层温度 pH 微观形貌 XRD
毕业论文外文摘要
Title Nickel-plated phosphor bronze ABS posite
Abstract
This study is in ABS plastic substrates for co-deposition of Ni-P-Cu to obtain a certain thickness with ic posite coatings. Main topics explores the plating temperature, pH and CuSO4 addition on the coating thickness, surface topography and other effects. By optical microscopy, SEM and XRD we analysis the Ni-P-posite coating about the Micro – morphology and coating phase, the results showed that:On the basis of nickel-phosphorus plating bath when CuSO4 content of 4g/L, temperature 80℃, we can get homogeneous cellular coating and with strong substrate on the ABS, the same time it pletely covering the surface of the substrate, XRD analysis shows that the coating of amorphous nickel-phosphorus "bread peak" superimposed the Cu alloy (200),(220) Crystal face diffraction peaks. Indicate the ABS matrix get co-deposition of Ni-P-posite coating by the optimized process and confirmed the formation and growth of the coating is cell packing of spheres growth mechanism.
Key Words ABS substrate Ni-P-posite coating Temperature PH Micro – morphology XRD
目录
1 简介 1
课题的研究背景及其意义 1
ABS塑料简介 1
ABS塑料化学复合镀简介 2
电磁屏蔽 5
ABS化学镀发展现状及展望 5
2 实验方案与设备 7
实验方案与路线 7
主要设备及操作 8
3 实验过程 12
4 分析与讨论 17
温度对施镀过程的影响 17
PH对施镀过程的影响 17
硫酸铜加入量对施镀过程的影响 18
镀层形貌分析 18
结论 22
致谢 23
参考文献 24
1 简介
课题的研究背景及其意义
ABS是本世纪40年代发展起来的通用热塑性工程塑料,是一个综合力学性能十分优秀的塑料品种,不仅具有良好的刚性、硬度和加工流动性,而且具有高韧性特点,可以注塑、挤出或热成型。ABS塑料作为用量最大的工程塑料之一,其抗冲击性、耐热性、耐低温性、耐化学药品性及电气性能优良,还具有易加工、制品尺寸稳定、表面光泽性好等特点,容易涂装、着色,还可以进行表面喷镀金属、电镀、焊接、热压和粘接等二次加工,由于其自身的组成