摘要:硅烷掺杂(改性)防护性聚合物涂层是制备新型环保涂层的一种新方法。它摒弃了传
统涂层的环境毒性和高成本而具有重要现实意义。本文较详细地介绍了这种新型涂层的制备
方法及硅烷促进聚合物涂层抗蚀性能的作用原理。
关键词:防腐蚀;硅烷;聚合物涂层;掺杂改性
中图分类号:TG178
Research progress in silane-modified anticorrosive
polymeric coatings
JIANG Meiyan, WU Liankui, HU Jiming
(Department of Chemistry, Zhejiang University, Hangzhou 310027)
Abstract: In recent years, a rapid surge of the novel "green" polymer coating based on the silane
modification has been found its in the field of corrosion control of metals. It has a great realistic
significance to discarding toxicity and expensive manufacturing technology. In this paper, the
modification of polymer coating by silane is reviewed in details.
Key words: Corrosion protection; silane; polymeric coating; modification
0 引言
尽管已经发开出各种新型防护技术,有机涂层仍是金属构件腐蚀防护的主要手段。传统
的涂装体系一般需要经过多道特点和功效各异的涂装工序处理,同时掺杂多种缓蚀性的颜、
填料[1-6],如铅盐、铬酸盐、磷酸盐等。这不仅提高了涂装成本,造成工序繁琐,另一个致
命缺点是生物毒性强、环境污染大。众所周知,六价铬酸盐和重金属铅、锌盐对生物体有很
大毒性,而磷酸盐则会引起水体富营养化。因此,开发新型环保涂层技术已成为当今国内外
腐蚀工作者的研究热点。
金属硅烷化(Silanization)工艺的出现是近年来环保型金属防护预处理领域的技术革新
30
[7-11]
。基于环境友好型烷基硅氧烷制备的硅烷膜[3,12-26],既可单独作为预防护层对金属起到
短期防护作用,又可作为表面转化层,起到提高后续涂覆的有机涂层与基体结合力的作用,
有望取代目前常用的磷化层或铬酸盐转化层。一般,硅烷sol-gel成膜过程主要包括:硅氧烷
试剂可水解的官能团发生水解生成硅醇;进而与金属表面羟基通过缩合反应生成Me-O-Si-
化学键,同时,硅醇间也可发生缩聚反应生成-Si-O-Si-结构。由于上述过程形成的具有较强
35
40
化学键合的Me-O-Si-共价键,且交联聚合产物膜-Si-O-Si-具有良