文档介绍：
熔盐电沉积法镀钛及镀层表征#
闫蓓蕾*
(攀钢集团研究院有限公司钒钛资源综合利用国家重点实验室)
5
10
摘要:本文介绍了熔盐电沉积方法在金属钼表面镀金属钛涂层的实验过程,进一步研究了工
艺过程参数熔盐温度 700℃~850℃、电流密度 ~ 对镀层性质的影响。通过
电化学测试得到,在熔盐电沉积过程中低价钛离子经历了一次还原过程得到金属钛。
关键词:电化学;熔盐;电沉积;低价钛离子
中图分类号:TQ [文献标识码]A
Electrodeposition of titanium in molten salt
YanBeilei
(Pan Gang Group Research Institute Co.,Ltd. , State Key Laboratory of Vanadium and Titanium
15
Abstract:
prehensive Utilization)
This article introduced the molten salt electrodeposition method in the metal molybdenum
titanium metallized coating the surface of the test process, further study on the process parameters, the
molten salt temperature 700 ℃~ 850 ℃, the current density of A/cm2 ~ A/cm2 effects on
coating properties. Through electrochemical testing, low titanium ion in the process of molten salts
20
25
30
35
electroplating experienced a reduction process of titanium.
Key words: Electrochemical, molten salt, Electro-deposition, Low-cost titanium ion.
0 引言
钛及钛基合金具有熔点高、密度小、强度大、耐腐蚀强等特点,是现代航空、火箭导弹
工业及航天技术的优良材料,优异的轻型结构材料、新型功能材料和重要的生物医用材料
[1-3]
序多、能耗高等因素,致使海绵钛成本居高不下,价格远高于钢铁的价格,单位重量价格也
是金属铝的3倍以上,严重限制了钛在各行业和各领域中的应用[4-5]。为了满足生产生活中对
钛材日益增长的的需求,并合理利用资源,以钛作为金属镀层的应用形式将是一种有前景的
途径。钛在热力学上是一种不稳定的金属,但是在大多数介质中,它显示出非常好的耐蚀性。
这是因为钛表面覆盖着致密、韧性的薄层氧化膜,保护基体处于钝化状态,即使是清理干净
的表面,当置于空气中或水溶液等含氧介质中时又很快重新生成新膜,这是钛耐腐蚀性能优
异的主要原因。但这层氧化膜使得钛上电镀难以进行,如果按照常规进行电镀,不能得到良
好的结合力。近年