文档介绍：摘要
本文采用冷态涂敷方法,用水玻璃和松香作黏结剂,在45钢表面涂敷了镍基自熔性合金粉末Ni60和Ni60+WC25,利用炉内加热和感应加热的方法对涂层进行了重熔处理,并对重熔试样进行了销盘式磨粒磨损实验;对重熔涂层进行了显微硬度分析和金相组织分析,利用扫描电子显微镜(SEM)对涂层磨损后的形貌进行了分析。结果表明:重熔涂层具有很高的耐磨性,明显高于T10钢淬火后的试样;Ni60+WC重熔涂层的耐磨性稍高于Ni60重熔涂层;感应重熔涂层的耐磨性要高于炉内重熔的涂层;用松香作黏结剂的涂层稍高于用水玻璃作黏结剂的涂层;重熔涂层磨损表面的SEM形貌表明磨损属于磨粒磨损。
关键词:自熔性合金,感应重熔涂层,炉内重熔涂层,镍基WC,磨粒磨损
Abstract
Nickel base self-fluxed alloy powder Ni60 and Ni60+WC25 are spreaded on the surface of 45 steel by cold-state coating technique has been shown in this paper,the bonding agents use water glass and rosin,and the coatings are remelted using furnace and induction heating methods,the wear-resistant of the remelting coatings are investigated by the abrasive wear machine. The hardness and microstructure of the coatings are also analzyed,the worn surface morphology of the coatings are observed by electron scanning microscope(SEM). The results indicate that the remelting coatings have very high wear-resistant,and apparently higher than the quenched T10 sample. The wear-resistant of Ni60+WC25 remelting coatings are better than that of Ni60 coatings,and the induction remelting coatings are better than that of the furnace remelting coatings,also the remelting coatings of rosin bonding agents are better than that of water glass bonding agents coatings. The SEM morphology of the worn surface shown it belongs to abrasive wear.
Keywords:self-fluxed alloy, induction remelting coatings, furnace remelting coatings,WC nickel base,abrasive wear
毕业设计(论文)原创性声明和使用授权说明
原创性声明
本人郑重承诺:所呈交的毕业设计(论文),是我个人在指导教师的指导下进行的研究工作及取得的成果。尽我所知,除文中特别加以标注和致谢的地方外,不包含其他人或组织已经发表或公布过的研究成果,也不包含我为获得及其它教育机构的学位或学历而使用过的材料。对本研究提供过帮助和做出过贡献的个人或集体,均已在文中作了明确的说明并表示了谢意。
作者签名: 日期:
指导教师签名: 日期:
使用授权说明
本人完全了解大学关于收集、保存、使用毕业设计(论文)的规定,即:按照学校要求提交毕业设计(论文)的印刷本和电子版本;学校有权保存毕业设计(论文)的印刷本和电子版,并提供目录检索与阅览服务;学校可以采用影印、缩印、数字化或其它复制手段保存论文;在不以赢利为目的前提下,学校可以公布论文的部分或全部内容。
作者签名: 日期:
学位论文原创性声明
本人郑重声明:所呈交的论文是本人在导师的指导下独立进行研究所取得的研究成果。除了文中特别加以标注引用的内容外,本论文不包含任何其他个人或集体已经发表或撰写的成果作品。对本文的研究做出重要贡献的个