文档介绍：沥青混合料力学特性的时温依赖性研究
肖月,李立斌,李强
(南京林业大学土木工程学院,江苏南京 210037)
摘要:采用动态模量试验、抗压强度试验以及劈裂试验在不同时间和温度条件下对三种沥青混合料力学特性的时温依赖性进行了分析。结果表明:在线弹性以及大变形条件下其均满足时温等效原理,并建立了不同力学参数的主曲线。
关键词:沥青混合料,强度,主曲线,时温等效原理
中图分类号:U416. 217 文献标志码: A
Time-temperature dependency of mechanical parameters for asphalt mixtures
XIAO Yue, LI Li-bin, LI Qiang
(School of Civil Engineering,Nanjing Forestry University, Nanjing 210037)
Abstract: The time-temperature dependency of mechanical parameters for three types of asphalt mixtures was evaluated using dynamic modulus test, compressive strength test and splitting test at different time and temperature conditions. It is found that they can satisfy the time-temperature superposition principle at linear elastic and large deformation conditions. Their master curves were also obtained.
Key words: asphalt mixture, strength, master curve, time-temperature superposition principle
0 引言
沥青混合料是一种典型的黏弹性工程材料,其力学行为对于加载时间和温度具有明显的依赖性[1-2]。目前大多数强度试验根据经验选用的变形速率为50 mm/min,尚未有研究表明它与现场道路情况相符。况且,不同路况和车况条件下行车速度千变万化,不同路面深度处的应变和承受的脉冲荷载持续时间也不同。这就说明,采用单一应变率水平的强度试验并不能准确地模拟实际路面内复杂而又不停变化的受力状态。因此,有必要在不同时温条件下对沥青混合料力学性能的时温依赖性进行研究,并应用时间-温度等效原理建立其主曲线,从而可以更为准确和简便地描述材料在较大应变率和温度变化范围内的性能。
1 试验方案
采用三种常用的沥青混合料进行室内试验,分别定义为AC-20C(AC-20级配+70#普通沥青)、AC-20M(AC-20级配+SBS改性沥青)和SMA-13C(SMA-13级配+70#普通沥青)。矿料级配见表1。%、%%。
表1 沥青混合料级配组成
级配
通过率/%
19 mm
mm
mm
mm